Consider a material with a tensile strength of 420 MPa, and elastic limit of 310 MPa. What is the maximum load capable of being supported with out breaking by supported by wire of radius of 2.5 mm?
A = Area of cross-section = r2 = 3.14
(0.0025)2 = 0.000019625
F = weight
F/A = 420 x 10^6
F = 420 x 10^6 (0.000019625)
F = 8242.5 N
Consider a material with a tensile strength of 420 MPa, and elastic limit of 310 MPa....
(20%) Question 6. The elastic modulus, yield strength and ultimate strength of a certain material afe 110 GPa 2400 MPa and 265 MPal respectively. If a cylindrical bar of this material 380 mm long is subjected to a uniaxial tension test and its length is increased by an amount áf O.50 mm under a tensile load ót 6660 N.At the same time its diameter decreased by0,28 mm Calculate; a) The initial diameter of the bar, (8%) d b) Under an...
The leakage limit of an aluminum alloy to uniaxial
tensile is Y = 320 MPa. The same material also leaks into a complex
load described by the tensile state [σij]:
Consider what leakage criterion (Treska or Mises) best describes the behavior of the material.330 95 0 Съ-| 95 70 01 MPa 00150
3 (15 points) A bent circular cantilever beam of uniform diameter of 25 mm is shown in igure below. The beam is made from a material with elastic modulus is 70 GPa, the tensile strength is 250 MPa, and the ultimate strength is 300 MPa. 250 mm A. 150 mm z Zz. 50N V (z direction) 100 N (a) (5 points) What are the stresses in the beam at point A? (b) (10 points) Based on your calculations in (a),...
A shaft is to be manufactured from a steel having an ultimate tensile strength of 420 MPa, and a yield stress of 305 MPa. The shaft has a solid circular cross section of diameter 50 mm and is subjected to a sinusoidally varying torque ranging from 60 Nm to 130 Nm. It has also been established that the shaft has a fully-corrected endurance limit of 129 MPa and that a torsional fatigue stress concentration factor, kf = 2.1, exists at...
1-Determine the % elongation, yield stress and ultimate tensile
strength of the material tested above
2-Calculate the elastic modulus of the material tested above
3-If a 200mm cylindrical rod of the material tested above, with
radius 20mm, was subjected to a tensile load of 200kN, what would
the length be?
4-An underground wastewater steel pipe with 2mm walls carries an
ammonia solution of 40 g/m3. The pipe is in contact with
groundwater (assume 0 g/m3 ammonia). Determine the
diffusion rate...
2. (10 points) Low carbon steel having a tensile strength 300 MPa and a shear strength 220 MPa is turned at a cutting speed 2.5 m/s. Feed 0.20 mm/rev and depth of cut 3.0 mm. The rake angle 5° in the direction of chip flow. The resulting chip ratio 0.45. Using the orthogonal model to approximate turning, determine (a) the cutting force, (b) thrust force, (c) the friction angle, and (d) material removal rate RMR 73 V2.r d3n -S
I. (SI units) Low-carbon steel with tensile strength-300 MPa, shear strength-220 MPa, and Brinell hardness of 225 HB is turned at a cutting speed-2.5 m/s. Feed-0.20 mm/rev and depth of cut- 3.0 mm. Rake angle - 5° in the direction of chip flow. The resulting chip ratio 0.45. Using the orthogonal model to approximate turning, determine (a) cutting force, (b) feed force, and (c) compute the required power, if mechanical efficiency-80%. (30 points) (Hint: correction factor for the volume specific...
I. (SI units) Low-carbon steel with tensile strength-300 MPa, shear strength-220 MPa, and Brinell hardness of 225 HB is turned at a cutting speed-2.5 m/s. Feed-0.20 mm/rev and depth of cut- 3.0 mm. Rake angle - 5° in the direction of chip flow. The resulting chip ratio 0.45. Using the orthogonal model to approximate turning, determine (a) cutting force, (b) feed force, and (c) compute the required power, if mechanical efficiency-80%. (30 points) (Hint: correction factor for the volume specific...
If my material has an ultimate tensile strength of 52 KSU, yield strength of 35 ksi, elastic modulus of 6.5 msi, and a poisssons ratio of 0.33. What is the maximum force that can be reached till failure?
A stepped shaft with a ground finish is made of steel with an ultimate tensile strength of 1200 MPa. The shaft is loaded with a fully reversed torque of 20 Nm. Dimensions of the shaft are given below. (5) a) Given the stress concentration for fatigue loading, Kfs 1.3, find the location and magnitude of the maximum stress in the shaft. (14) b) Find the endurance limit, assuming room temperature and a reliability of 99%. (1) c)Will the part have...