A 8.9-mm-diameter rod of 3003-H14 aluminum alloy with an elastic modulus of 58MPa and a poisson's...
A 7.3-mm-diameter rod of 3003-H14 aluminum alloy with an elastic modulus of 51MPa and a poisson's ratio of 0.3 is subjected to a 4-KN tensile load. Calculate the resulting rod diameter to 5 significant figures. Answer:
Q-1 A solid circular rod with a diameter d = 18 mm is shown in Figure Q-3. The rod is made of an aluminum alloy that has an elastic modulus E = 72 GPa and a Poisson's ratio v=0.32. When subjected to the axial load P, the diameter of the rod decreases by 0.025 mm. For a factor of safety of 1.75, a) Determine the magnitude of the safe allowable load P. pts.] b) If we have a 12 mm...
on 5 Consider a cylindrical specimen of some hypothetical metal alloy that has a diameter of 10.0 mm. A tensile force of 1500 N produces an elastic reduction in diameter of 6.7 x 10 mm. Compute the elastic modulus of this alloy, given that Poisson's ratio is 0.35. Express the answer in GPa to three significant figures. 5.00 out Answer: 99.8 Lion
Q1. A circular rod of 12 mm diameter was tested for tension. The total elongation on a 300 mm length was 0.22 mm under a tensile load of 17 KN. Find the value of E. (2.5 Marks) Answer: Q2. A prismatic bar has a cross section of 25 mm x 50 mm and a length of 2m under an axial force of 90 KN. The measured elongation of the bar is 1.5 mm. Compute the tensile stress and strain in...
According to machine elements 1 Q-1 A solid circular rod with a diameter d= 18 mm is shown in Figure Q-3. The rod is made of an aluminum alloy that has an elastic modulus E = 72 GPa and a Poisson's ratio v = 0.32. When subjected to the axial load P, the diameter of the rod decreases by 0.025 mm. For a factor of safety of 1.75, a) Determine the magnitude of the safe allowable load P. [18 pts.]...
6 6.19 Consider a cylindrical specimen of some hypothetical metal alloy that has a diameter of 8.0 mm (0.31 in), A tensile force of 1000 N (225 lb) produces an elastic reduction in diameter of 2.8 x 101mm (1.10 x10 in,). Compute the modulus of elasticity for shis alloy, given that Poisson's ratio is 0.30
rn A specimen of copper having a rectangular cross section 15.2 mm x 19.1 mm is pulled in tension with 44,500 N force, producing only elastic deformation. Calculate the resulting strain. Round off the answer to three significant figures. Answer: 1.394e-3 A cylindrical specimen of a nickel alloy having an elastic modulus of 207 GPa and an original diameter of 10.2 mm experiences only elastic deformation when a tensile load of 8900 N is applied. Compute the maximum length of...
Problem #1 A cylindrical rod of copper (E 110 GPa) having a yield strength of 240 MPa is to be subjected to a load of 6660 N. If the length of the rod is 380 mm, what must the diameter be to allow an elongation of 0.50 mm? A cylindrical specimen of some alloy 8 mm in diameter is stressed elastically in tension. A force of 15,700 N produces a reduction in the specimen diameter of 5 10-3 mm. Compute...
A cylindrical specimen of some metal alloy having an elastic modulus of 121 GPa and an original cross-sectional diameter of 4.7 mm will experience only elastic deformation when a tensile load of 2400 N is applied. Calculate the maximum length of the specimen before deformation if the maximum allowable elongation is 0.41 mm.
A cylindrical specimen of some metal alloy having an elastic modulus of 120 GPa and an original cross-sectional diameter of 3.0 mm will experience only elastic deformation when a tensile load of 2400 N is applied. Calculate the maximum length of the specimen before deformation if the maximum allowable elongation is 0.47 mm.