Given the crystal structure of Zn is HCP (a = 266.49 pm, c = 494.68 pm):...
Given the crystal structure of Zn is HCP (a = 266.49 pm, c = 494.68 pm):
(a) Determine the slip system(s) based on the given information.
(b) Estimate the Peierls-Nabarro Stress for given that G = 43 GPa, and ?=0.25.
Homework Answers
1) Since Zinc has a HCP structure. So no of slip system for a HCP structure is = 3.
2) G = 43 GPa, v = .25,. a = 266.49pm,. c = 494.68pm
Add Answer to:
Given the crystal structure of Zn is HCP (a = 266.49 pm, c =
494.68 pm):...
1. For zine (Zn) with a perfect HCP crystal structure having a c/a ratio of 1.633...
1. For zine (Zn) with a perfect HCP crystal structure having a c/a ratio of 1.633 and a density of 7.13 g/cm, (18 marks) a) Show that the volume of the Zn unit cell is given by 6v3R2c. (10 marks) b) Compute the atomic radius for Zn in nm. (8 marks)
1. For zinc (Zn) with a perfect HCP crystal structure having a c/a ratio of 1.633 and a density of 7.13 g/cm'. (18...
1. For zinc (Zn) with a perfect HCP crystal structure having a c/a ratio of 1.633 and a density of 7.13 g/cm'. (18 marks) a) Show that the volume of the Zn unit cell is given by 6V3R'C. (10 marks) b) Compute the atomic radius for Zn in nm. (8 marks)
1. A single crystal sample of a metal with a HCP structure is subjected to an axial tensile force. The sample is of circ...
1. A single crystal sample of a metal with a HCP structure is subjected to an axial tensile force. The sample is of circular cross-section, with a diameter of 4 mm, and is of 50 mm length. An elastic extension of 0.047 mm is measured when an axial tensile force of 1.25 kN is applied. When the tensile force is increased to 2.8 kN plastic deformation commences. (a) Given that Poisson’s ratio for the metal is 0.35, estimate the theoretical...
Magnesium has the HCP crystal structure. Given the data from the previous problem and the fact...
Magnesium has the HCP crystal structure. Given the data from the previous problem and the fact that we can take the lattice constant in the c-direction to be 0.497, what is the planar packing factor for the (10 -1 0) (... forgive the formating as I cannot do an overbar here) plane?
(1) A crystalline grain of iron (BCC crystal structure) in a metal plate is situated so that a te...
(1) A crystalline grain of iron (BCC crystal structure) in a metal plate is situated so that a tensile stress is applied along the [110] crystal direction of the grain, if slip occurs on a (101) plane and a [111] direction, determine the amount of tensile stress that is required to produce a critical resolved shear stress of 31.1MPa in the grain? [15 points] (2) Draw the unit cell structure, and on your sketch indicate: (i) the tensile direction, (ii)...
Iron titanate, FeTiO3, forms in the ilmenite crystal structure that consists of an HCP arrangement of...
Iron titanate, FeTiO3, forms in the ilmenite crystal structure that consists of an HCP arrangement of 02- ions. (a) Which type of interstitial site will the Fe2+ ions occupy? sites (b) Which type of interstitial site will the Ti4+ ions occupy? sites (c) What fraction of the total tetrahedral sites will be occupied? (In decimal form to two places to the right of the decimal) (d) What fraction of the total octahedral sites will be occupied? (In decimal form to...
A single crystal in the form of a cube has two possible slip planes. (1) and...
A single crystal in the form of a cube has two possible slip planes. (1) and (2). as shown in the sketch below. Each of these planes has two possible slip directions, (a) and (b), as is also shown. The angle between the tensile load axis and slip plane normal for both slip planes is 450 40 <plane (1)> <plane (2)> a) If a stress is applied to this crystal in the direction noted, specify which particular (eg. plane (1),...
20 points. The frictional shear stress to move a dislocation through a perfect crystal is given...
20 points. The frictional shear stress to move a dislocation through a perfect crystal is given by Ti = G exp((-2nd / b(1-v)) where d is the atomic spacing on close packed plane and b is the magnitude of the Burgers vector. Calculate ty for an fcc Cu crystal, if the dislocation is a Shockley partial. The shear modulus Cu is 42 GPa, its Poisson's ratio is 0.3, and its lattice parameter is 3.618.
For the reaction Zn(s) + Cla) -- 2ZnCl2 (s) given the following information: S [Cl2(g)] =...
For the reaction Zn(s) + Cla) -- 2ZnCl2 (s) given the following information: S [Cl2(g)] = +215.0 J/mol K, S [Zn(s) - 41.2 l/mol K and SIZnCl2631 = +107.1 J/mol K a) Determine AS (10 p) b) Determine the AG*rn of ZnCl2() if the AH- -409.1 kJ/mol, at 25°C (10p) c) Determine the AG on for the preparation of 11 g of ZnCl2l) (MM= 136.30 g/mol) (10p)
Q2. Atomic radius, crystal structure, electronegativity, and the most common valence are given in the following...
Q2. Atomic radius, crystal structure, electronegativity, and the most common valence are given in the following table for several elements: for those that are nonmetals, only atomic radii are indicated. Atemic Radias (nm) Electro- negativity Crystal Stractare Which of these elements would you expect to form the following with nickel: (a) a substitutional solid solution having Valence Element +2 18 FCC 0.1246 Ni. 0,071 C complete solubility (b) a substitutional solid solution of incomplete solubility 0.046 0.060 +1 1.9 0.1445...
1. For zine (Zn) with a perfect HCP crystal structure having a c/a ratio of 1.633 and a density of 7.13 g/cm, (18 marks) a) Show that the volume of the Zn unit cell is given by 6v3R2c. (10 marks) b) Compute the atomic radius for Zn in nm. (8 marks)
1. For zinc (Zn) with a perfect HCP crystal structure having a c/a ratio of 1.633 and a density of 7.13 g/cm'. (18 marks) a) Show that the volume of the Zn unit cell is given by 6V3R'C. (10 marks) b) Compute the atomic radius for Zn in nm. (8 marks)
(1) A crystalline grain of iron (BCC crystal structure) in a metal plate is situated so that a tensile stress is applied along the [110] crystal direction of the grain, if slip occurs on a (101) plane and a [111] direction, determine the amount of tensile stress that is required to produce a critical resolved shear stress of 31.1MPa in the grain? [15 points] (2) Draw the unit cell structure, and on your sketch indicate: (i) the tensile direction, (ii)...
Iron titanate, FeTiO3, forms in the ilmenite crystal structure that consists of an HCP arrangement of 02- ions. (a) Which type of interstitial site will the Fe2+ ions occupy? sites (b) Which type of interstitial site will the Ti4+ ions occupy? sites (c) What fraction of the total tetrahedral sites will be occupied? (In decimal form to two places to the right of the decimal) (d) What fraction of the total octahedral sites will be occupied? (In decimal form to...
A single crystal in the form of a cube has two possible slip planes. (1) and (2). as shown in the sketch below. Each of these planes has two possible slip directions, (a) and (b), as is also shown. The angle between the tensile load axis and slip plane normal for both slip planes is 450 40 <plane (1)> <plane (2)> a) If a stress is applied to this crystal in the direction noted, specify which particular (eg. plane (1),...
20 points. The frictional shear stress to move a dislocation through a perfect crystal is given by Ti = G exp((-2nd / b(1-v)) where d is the atomic spacing on close packed plane and b is the magnitude of the Burgers vector. Calculate ty for an fcc Cu crystal, if the dislocation is a Shockley partial. The shear modulus Cu is 42 GPa, its Poisson's ratio is 0.3, and its lattice parameter is 3.618.
For the reaction Zn(s) + Cla) -- 2ZnCl2 (s) given the following information: S [Cl2(g)] = +215.0 J/mol K, S [Zn(s) - 41.2 l/mol K and SIZnCl2631 = +107.1 J/mol K a) Determine AS (10 p) b) Determine the AG*rn of ZnCl2() if the AH- -409.1 kJ/mol, at 25°C (10p) c) Determine the AG on for the preparation of 11 g of ZnCl2l) (MM= 136.30 g/mol) (10p)
Q2. Atomic radius, crystal structure, electronegativity, and the most common valence are given in the following table for several elements: for those that are nonmetals, only atomic radii are indicated. Atemic Radias (nm) Electro- negativity Crystal Stractare Which of these elements would you expect to form the following with nickel: (a) a substitutional solid solution having Valence Element +2 18 FCC 0.1246 Ni. 0,071 C complete solubility (b) a substitutional solid solution of incomplete solubility 0.046 0.060 +1 1.9 0.1445...
Most questions answered within 3 hours.
-
Work out a care plan for Rex to help her better manage
her medical conditions. Provide...
asked 23 seconds from now -
The historical returns on a balanced portfolio have had an
average return of 11% and a...
asked 4 minutes ago -
Sulfuric acid (250.0mL) is titrated with 176.5 mL 2.4 M NaOH to
an equivalence point (the...
asked 16 minutes ago -
The quality control manager of a cookie company is inspecting a
batch of chocolate-chip cookies that...
asked 17 minutes ago -
How can we identify what the horizontal force is when looking at
a merry go round?...
asked 49 minutes ago -
While Dime Community Bank is based in Brooklyn; management has
decided to focus its lending activity...
asked 1 hour ago -
1) Earnings functions, whereby the log of earnings is regressed
on years of education, years of...
asked 48 minutes ago -
Bruno Corporation is involved in the business of injection
molding of plastics. It is considering the...
asked 53 minutes ago -
What would be the vapor pressure of water at 96°C above a
solution made by dissolving...
asked 1 hour ago -
Hydration of norbornene
Write the reaction. Discuss the intermediate. Explain how the
equilibrium in the reaction...
asked 1 hour ago -
Suppose that a party wanted to enter an FRA that expires in 42
days and is...
asked 1 hour ago -
ABC Ltd. estimated that a new store requires an initial
investment of $800,000. This new store...
asked 1 hour ago