Copper and nickel can be mixed to form a corrosion-resistant alloy. If a particular alloy is prepared by mixing 9.40 moles of copper with 1.60 moles of nickel, what is the mass percentage of nickel in the alloy?
Copper and nickel can be mixed to form a corrosion-resistant alloy. If a particular alloy is...
cooper and nickel can be mixed to form a corrosion resistant alloy. if a particular alloy is prepared by mixing 13.7 moles of cooper with 1.00 moles of nickel. what is the mass percentage of nickel in the alloy
A copper-nickel (35 wt % - 65 wt %) alloy is corroded in an oxygen-concentration cell using boiling water. What volume of oxygen gas (at 1 atm) must be consumed at the cathode to corrode 54 g of the alloy? (Assume only divalent ions are produced.) Express your answer to three significant figures.
A 2.50 g sample of bronze was dissolved in sulfuric acid. The copper in the alloy reacted with sulfuric acid as follows: Cu(s) + 2H2SO4 (aq) → CuSO4 (aq) + SO2(g) + 2 H20 (1) The CuSO4 formed in the reaction was mixed with Kl to form Cul (copper iodide). 2 CuSO4 (aq) + 51 → 2 Cul (s) + 1; (aq) + 2 So(aq) The formed in that reaction was then titrated with (aq) + 2 5,03 – 31...
An alloy is 11.1% copper by mass in tin. Copper makes up what percentage of the atoms in this sample?
Brass is a metallic alloy of copper and zinc. The relative percentages of copper and zinc determine the properties of the brass; resistance to corrosion and malleability, for example, are dependent on the relative amounts of copper and zinc. The percentage of zinc within a sample of brass may be determined using the techniques encountered in this experiment. 1. A 0.3400 g piece of brass is allowed to react with hydrochloric acid at the base of eudiometer. The hydrogen gas...
A copper-nickel alloy of composition (40% Ni-60% Cu) is slowly heated from a temperature of 1200°C: 1. a) At what temperature does the first liquid phase form? b) What is the composition of this liquid phase? c) At what temperature does complete melting of the alloy occur? d) What is the composition of the last solid remaining prior to complete melting? Composition (at% N) 100 0 1600 2800 1500 1453°C Liquid 2600 Soldus line Liquidus line 1300 - 2200 120아ㅡㅡㅡㅡㅡ...
Red gold is a gold‑copper alloy used to make jewelry. A piece of jewelry made of red gold weighs 8.35 g and has a volume of 0.581 cm3. Gold has a density of 19.3 g/cm3 and copper has a density of 8.96 g/cm3. Calculate the percentage by mass of each metal in the jewelry. Assume the total volume of the jewelry is the sum of the volumes of the two metals it contains. gold: % : copper: % : Pure...
Red gold is a gold-copper alloy used to make jewelry. A piece of jewelry made of red gold weighs 8.40 g and has a volume of 0.604 cm?. Gold has a density of 19.3 g/cm² and copper has a density of 8.96 g/cm². Calculate the percentage by mass of each metal in the jewelry. Assume the total volume of the jewelry is the sum of the volumes of the two metals it contains. gold: copper: Pure gold is defined as...
Red gold is a gold‑copper alloy used to make jewelry. A piece of jewelry made of red gold weighs 8.80 g and has a volume of 0.594 cm3. Gold has a density of 19.3 g/cm3 and copper has a density of 8.96 g/cm3 . Calculate the percentage by mass of each metal in the jewelry. Assume the total volume of the jewelry is the sum of the volumes of the two metals it contains. gold: % copper: % Pure gold...
3. Modern quarters are clad coins with a copper-nickel alloy sandwiching a pure copper core. The specifications for legal tender quarters established by the U. S. Mint are very exacting 1) be 8.33% Ni by mass and the balance Cu 2) weigh 5.670 g 3) have diameter of 24.26 mm 4) a thickness of 1.75 mm Each coin must: Use this information in the following problems a. Use dimensional analysis to calculate the g Ni in YOUR quarter b. Nickel...