Question 1: Using the copper-silver phase diagram in Figure 1 a. What is the eutectic composition...
3. On Silver-Copper phase diagram, label the liquidus line, eutectic point, and all unlabeled regions. Also answer questions below a. How many phases are there? b. What is the eutectic temperature? c. What is the eutectic concentration (in mass percent)? d. What is the composition of the Ag in the solid solution at the eutectic temperature? e. What is the composition of the Cu in the solid solution at the eutectic temperature? f. At 600°C what is the composition of...
For a 70 wt % You are given the binary eutectic copper-silver phase diagram shown in Figure 2. Cu-30 wt% Ag alloy at a temperature of 1600°F, determine the following: . The phases present at the provided state point The weight percent of these phases along the tie line. The amounts of each of these phases at the state point. The degree(s) of freedom at the provided state point Atomic percent silver 30 40 50 60 70 80 90 10...
Question 4 (25 marks) (a) Consider the hypothetical eutectic phase diagram for metal for lead-tin system. Assume that (1) A and B phase cutectic phase diagram for metals A and B, which is similar to that 1. Assume that (1) a and B phases exist at the A and B extremities of the phase diagram, respectively; (2) the eutectic composi m, respectively; (2) the eutectic composition is 36 wt% A-64 wt% B; and (3) the composition of the a phase...
2. [25 points] The following figure shows the phase diagram of Cu-Ag alloy system. A mixture of Ag and Cu with a eutectic composition (or concentration) is heated to a high temperature and keep for enough time to prepare the material into a uniform liquid state. The material is then cooled down to 800°c. Cu-Ag System 1200 Liquid 800 A 600 400 100 80 60 40 20 wt% Ag a) What is the Ag composition in the original material so...
2. [25 points] The following figure shows the phase diagram of Cu-Ag alloy syst em. A mixture of Ag and Cu with a eutectic composition (or concentration) is heated to a high temperature and keep for enough time to prepare the material into a uniform liquid state. The material is then cooled down to 800°C. Cu-Ag System 1200p Liquid 1000 800 A B. 600 400 200 100 80 60 40 20 wt% Ag (o) What is the Ag composition in...
A copper-nickel alloy of composition (40% Ni-60% Cu) is slowly heated from a temperature of 1200°C: 1. a) At what temperature does the first liquid phase form? b) What is the composition of this liquid phase? c) At what temperature does complete melting of the alloy occur? d) What is the composition of the last solid remaining prior to complete melting? Composition (at% N) 100 0 1600 2800 1500 1453°C Liquid 2600 Soldus line Liquidus line 1300 - 2200 120아ㅡㅡㅡㅡㅡ...