Q2 What are the phases present at room temperature for steel of 0.76% C? Determine the...
Q2 What are the phases present at room temperature for steel of 0.76% C? Determine the composition & amounts of ferrite (a) and cementite (Fe3C) at room temperature in pearlite of eutectoid composition (0.76%C). Use attached Fe-Fe3C phase diagram or Fig. 9.24 in your text book. Composition (at% C) 10 25 1538°C TT - 1493°C 14008 1394°C 1147°C 4.30 y Austenite Temperature (°C) 1000 912°C y + Fezc 800 727°C 0.76 brol 600 0.022 a, Ferrite a + Fea Cementite...
You have a 1.8 kg sample of austenite containing 0.13 wt% C and it is cooled...
You have a 1.8 kg sample of austenite containing 0.13 wt% C and
it is cooled to less than 727°C (1341°F). The proeutectoid phase is
??ferrite.
(a) How many kilograms each of total ferrite and cementite
form?
___ kg of ferrite, ___ kg of Fe3C
(b) How many kilograms each of pearlite and the proeutectoid
phase form?
___ kg of proeutectoid ferrite, ___ kg of pearlite
composition wt% C Composition at% C Temperature 400 °C 1 Temperature-752 Composition (at% C)...
Problem 9.70 (GO Tutorial) Consider 2.6 kg of a 99.4 wt% Fe-0.6 wt% C alloy that...
Problem 9.70 (GO Tutorial) Consider 2.6 kg of a 99.4 wt% Fe-0.6 wt% C alloy that is cooled to a temperature just below the eutectoid. The iron-iron carbide phase diagram is shown in the Animated Figure 9.24 (a) How many kilograms of proeutectoid ferrite form? kg [The tolerance is +/- 2.0%.] (b) How many kilograms of eutectoid ferrite form? kg [The tolerance is +/- 2.0%.] (c) How many kilograms of cementite form? kg [The tolerance is +/- 2.0%.] Composition =...
15. From the iron-carbon phase diagram (see Figure below) a. What are the concentrations of carbon...
15. From the iron-carbon phase diagram (see Figure below) a. What are the concentrations of carbon in each a-ferrite and Fe3C at a temperature just below 727°C? b. What are the phases involved in the eutectoid reaction? c. I am making a hyper-eutectoid steel with 2 wt%C. If I cool slowly from 1400°C, what phases and microstructure will I have at room temperature, assuming only equilibrium phases can be present? d. What is the euctectoid composition for Fe-C system shown...
(12 Question 4: points: 4 pts each) Consider 3.0 kg of austenite containing 1.6 wt% C...
(12 Question 4: points: 4 pts each) Consider 3.0 kg of austenite containing 1.6 wt% C at 1100 °C, cooled to below 726 °C. (a) What is the proeutectoid phase? (b) How many kilograms of total ferrite and cementite form? (c) How many kilograms each of pearlite and the proeutectoid cementite form? Composition (at% C) 10 15 5 20 25 0 1600 1538°C 1493°C L 1400 S 1394°C 7+L 1200 1147°C 2.14 4.30 y, Austenite Temperature (°C) 1000 912°C y...
The phase diagram for the iron-carbon Fe-C system is shown below. use it to answer the...
The phase diagram for the iron-carbon Fe-C system is shown
below. use it to answer the following questions
a) How many different solid allotropes (phases) does pure iron
have?
b) what is the maximum carbon solubility of carbon in
austentite?
c) what is the maximum carbon solubility of carbon in
ferrite?
d)On cooling the following phase reaction occurs at 0.76% C and
727*c y--> alpha + Fe3C. On cooling what phase reaction occurs
at .16% C and 1493*c?
e)For a...
please answer question 2,3,4 A critical feature of steel is that a considerable amount of...
please answer question 2,3,4
A critical feature of steel is that a considerable amount of carbon can be dissolved in the austenite, phase, (up to 2.14 w/o at 1147"C), whereas carbon is essentially insoluble in ferrite, Cooling from point d to e, just above the eutectoid but still in the an increased fraction of the +y region, will produce phase and a microstructure similar to that shown: the particles precinitates out in the form af an intermetallic.compound called iron-carbide...
T(°C) Fe-C system 1600 & 1400 LI Y Y 1200 + t+Fec y+Fe20 (austenite) 1000 -...
T(°C) Fe-C system 1600 & 1400 LI Y Y 1200 + t+Fec y+Fe20 (austenite) 1000 - (FCC) 800 20.76 0.022 600 FezC (cementite) 727°C = Teutectoid a+Fe,c 0 2 3 4 5 (Fe) + 6.7 C, wt% C Consider a 10 kg hypereutectoid steel containing 1.5 wt% C at 850 °C (point A). If it is cooled just below the eutectoid temperature, how many kilograms of proeutectoid ferrite form?
When the steel containing 3.0wt% carbon is quenched very quickly (over 5000°C /s) from 1000 °C to...
When the steel containing 3.0wt% carbon is quenched very quickly
(over 5000°C /s) from 1000 °C to room temperature, what are the
phases present at room temperature after
quenching? Please explain why in
detail.
1600 1538°C 1493°C 1400 1394°C 1200 1147°C 2.14 4.30 y, Austenite 1000 912°C y+Fe3C 800 a 727°C 0.76 0.022 a, Ferrite 600 a Fe3C Cementite (Fe3C) 400 0 (Fe) 2 3 4 6.7 Composition (wt% C) The above shows the iron-carbon phase diagram in weight %...
please explain with the figure 2 A plain plain carbon steel of unknown composition is cooled...
please explain with the figure
2 A plain plain carbon steel of unknown composition is cooled in the furnace from w oning temperature. At room temperature, the percentage of primary (proeutectoid) ferrite() monin this steel is found to be 27%. Use Figure 1 and answer the following questions. What is the concentration of carbon present in this steel? b) Which other phase or phases will you find in the structure of this steel? c) Calculate the amount of the phase...
Q2 What are the phases present at room temperature for steel of 0.76% C? Determine the composition & amounts of ferrite (a) and cementite (Fe3C) at room temperature in pearlite of eutectoid composition (0.76%C). Use attached Fe-Fe3C phase diagram or Fig. 9.24 in your text book. Composition (at% C) 10 25 1538°C TT - 1493°C 14008 1394°C 1147°C 4.30 y Austenite Temperature (°C) 1000 912°C y + Fezc 800 727°C 0.76 brol 600 0.022 a, Ferrite a + Fea Cementite...
You have a 1.8 kg sample of austenite containing 0.13 wt% C and
it is cooled to less than 727°C (1341°F). The proeutectoid phase is
??ferrite.
(a) How many kilograms each of total ferrite and cementite
form?
___ kg of ferrite, ___ kg of Fe3C
(b) How many kilograms each of pearlite and the proeutectoid
phase form?
___ kg of proeutectoid ferrite, ___ kg of pearlite
composition wt% C Composition at% C Temperature 400 °C 1 Temperature-752 Composition (at% C)...
Problem 9.70 (GO Tutorial) Consider 2.6 kg of a 99.4 wt% Fe-0.6 wt% C alloy that is cooled to a temperature just below the eutectoid. The iron-iron carbide phase diagram is shown in the Animated Figure 9.24 (a) How many kilograms of proeutectoid ferrite form? kg [The tolerance is +/- 2.0%.] (b) How many kilograms of eutectoid ferrite form? kg [The tolerance is +/- 2.0%.] (c) How many kilograms of cementite form? kg [The tolerance is +/- 2.0%.] Composition =...
15. From the iron-carbon phase diagram (see Figure below) a. What are the concentrations of carbon in each a-ferrite and Fe3C at a temperature just below 727°C? b. What are the phases involved in the eutectoid reaction? c. I am making a hyper-eutectoid steel with 2 wt%C. If I cool slowly from 1400°C, what phases and microstructure will I have at room temperature, assuming only equilibrium phases can be present? d. What is the euctectoid composition for Fe-C system shown...
(12 Question 4: points: 4 pts each) Consider 3.0 kg of austenite containing 1.6 wt% C at 1100 °C, cooled to below 726 °C. (a) What is the proeutectoid phase? (b) How many kilograms of total ferrite and cementite form? (c) How many kilograms each of pearlite and the proeutectoid cementite form? Composition (at% C) 10 15 5 20 25 0 1600 1538°C 1493°C L 1400 S 1394°C 7+L 1200 1147°C 2.14 4.30 y, Austenite Temperature (°C) 1000 912°C y...
The phase diagram for the iron-carbon Fe-C system is shown
below. use it to answer the following questions
a) How many different solid allotropes (phases) does pure iron
have?
b) what is the maximum carbon solubility of carbon in
austentite?
c) what is the maximum carbon solubility of carbon in
ferrite?
d)On cooling the following phase reaction occurs at 0.76% C and
727*c y--> alpha + Fe3C. On cooling what phase reaction occurs
at .16% C and 1493*c?
e)For a...
please answer question 2,3,4
A critical feature of steel is that a considerable amount of carbon can be dissolved in the austenite, phase, (up to 2.14 w/o at 1147"C), whereas carbon is essentially insoluble in ferrite, Cooling from point d to e, just above the eutectoid but still in the an increased fraction of the +y region, will produce phase and a microstructure similar to that shown: the particles precinitates out in the form af an intermetallic.compound called iron-carbide...
T(°C) Fe-C system 1600 & 1400 LI Y Y 1200 + t+Fec y+Fe20 (austenite) 1000 - (FCC) 800 20.76 0.022 600 FezC (cementite) 727°C = Teutectoid a+Fe,c 0 2 3 4 5 (Fe) + 6.7 C, wt% C Consider a 10 kg hypereutectoid steel containing 1.5 wt% C at 850 °C (point A). If it is cooled just below the eutectoid temperature, how many kilograms of proeutectoid ferrite form?
When the steel containing 3.0wt% carbon is quenched very quickly
(over 5000°C /s) from 1000 °C to room temperature, what are the
phases present at room temperature after
quenching? Please explain why in
detail.
1600 1538°C 1493°C 1400 1394°C 1200 1147°C 2.14 4.30 y, Austenite 1000 912°C y+Fe3C 800 a 727°C 0.76 0.022 a, Ferrite 600 a Fe3C Cementite (Fe3C) 400 0 (Fe) 2 3 4 6.7 Composition (wt% C) The above shows the iron-carbon phase diagram in weight %...
please explain with the figure
2 A plain plain carbon steel of unknown composition is cooled in the furnace from w oning temperature. At room temperature, the percentage of primary (proeutectoid) ferrite() monin this steel is found to be 27%. Use Figure 1 and answer the following questions. What is the concentration of carbon present in this steel? b) Which other phase or phases will you find in the structure of this steel? c) Calculate the amount of the phase...
Most questions answered within 3 hours.
-
Oxidative phosphorylation is achieved through chemiosmotic
coupling, which turns chemical energy into osmotic potential energy
that...
asked 41 minutes ago -
Hollywood Shoes would like to maintain their cash account at a
minimum level of $64,000, but...
asked 40 minutes ago -
Proteins CtrA-P, DnaA, and GcrA behave similarly to what
molecule in the Eukaryotic Cell Cycle?
asked 44 minutes ago -
TRUE OR FALSE
In case of a competitive tender procedure, in the request for
quotation, the...
asked 52 minutes ago -
I am a little behind please provide some explanation, will
provide thumbs up.
This question considers...
asked 55 minutes ago -
Let say the utility function as U(X,Y) = lnX + Y. Show that the
marginal rate...
asked 1 hour ago -
A current of I=8.0A is flowing in a typical extension cord of
length L=3.00m. The cord...
asked 1 hour ago -
1. When balancing the equation H2SO4 (aq) + NaOH (aq) →
Na2SO4(aq) + H2O(aq), would you...
asked 1 hour ago -
Provide a definition of “classification hierarchy” and
illustrate your definition with an example of how and...
asked 1 hour ago -
1. Describe the four main green solvents. Provide one example of
the use of each solvent....
asked 1 hour ago -
International ethics focus on:
1) exploitation of labor
2)corruption
3) environmental impact
4) none of the...
asked 1 hour ago -
Costing Models You work for XYZ trucking and your boss has asked
you to figure out...
asked 1 hour ago