3. In the following phase diagram, determine (20 points): a. We are interested to design an alloy...
In the Al-Cu phase diagram, determine what phases are present in the binary areas (white area). Determine all the phase transformations happened in the following phase diagram. For a 20 wt% Cu alloy at 500 oC, determine: The phases present The phase compositions The fraction of each phase Draw microstructure of this alloy at 700 oC, 560 oC and 300 oC. We are interested to design an alloy with heat treatable characteristics. Please suggest a composition range and explain why?...
For a lead-tin alloy of composition Pb-30 wt.% Sn are heated to 300°C and slowly cooling down to room temperature. A Eutectic phase diagram of lead-tin alloy is shown in figure 3. What are the expected phases at 250°C, 150°C and at room temperature and estimate approximate phase fractions at these temperatures. Schematically draw the microstructures that would form at 250°C, 150°C and at room temperature. For a lead-tin alloy of composition Pb-30 wt.% Sn are heated to 300°C and...
Question 1: (16 points: 4 pts each) A 45 wt% Pb - 55 wt% Mg alloy is slowly cooled from 700°C to 400 °C. (a) At what temperature does the first solid phase form? (b) What is the composition of this solid phase? c) At what temperature does the liquid solidify? (d) What is the composition of this last remaining liquid phase? Composition (at% Pb) 10 20 30 40 70 100 700 L 600 L + MezPo M 500 400...
2. [25 points] The following figure shows the phase diagram of Cu-Ag alloy system. A mixture of Ag and Cu with a eutectic composition (or concentration) is heated to a high temperature and keep for enough time to prepare the material into a uniform liquid state. The material is then cooled down to 800°c. Cu-Ag System 1200 Liquid 800 A 600 400 100 80 60 40 20 wt% Ag a) What is the Ag composition in the original material so...
(12 Question 2: points: 4 pts each) For a Lead-Tin (Pb-Sn) alloy of composition 85 wt% Sn - 15 wt % Pb and at 182 °C determine the followings: Show your calculation details in your answer and draw lines on the phase diagram to label the phases and compositions. a) Determine the mass fractions of a and B phases. b) Determine the mass fractions of primary B and eutectic microconstituents. c) Determine the mass fraction of eutectic B. Composition (at%...
The following is the phase diagram for the lead-tin alloy: Pb-Sn Phase Diagram Composition (at% Sn) 100 300 500 200 83 C 61.9 97.8 300 100 100 100 Consider a lead-tin alloy containing 30 wt% Sn slowly (equilibrium) cooled from the liquid phase starting at 300°C. During this cooling process, the temperature of this alloy reaches 183.1° C (just above the eutectic temperature) and is held at this point of interest until equilibrium conditions are met. 1. (4 points) Draw...
2. [25 points] The following figure shows the phase diagram of Cu-Ag alloy syst em. A mixture of Ag and Cu with a eutectic composition (or concentration) is heated to a high temperature and keep for enough time to prepare the material into a uniform liquid state. The material is then cooled down to 800°C. Cu-Ag System 1200p Liquid 1000 800 A B. 600 400 200 100 80 60 40 20 wt% Ag (o) What is the Ag composition in...
4) Below is the phase diagram for Pb-Sn alloy. a) At 200 C°, determine the phases present at 10%Sn, 40%Sn and 80%Sn. (5 pts) b) At 200 C°, determine the composition of the phases for each weight percentage in (a). (5 pts) c) At 200 C°, determine the relative amount of each phase (weight fractions) for these points (5 pts) d) If you start cooling the system from 300 C° to 100 C°, what differences do you expect in the...
1. For the Cu-Zn phase diagram. For a 68 wt% Zn-32 wt% Cu alloy, list the phases and compositions that exist at 1000 °C, 760 °C, 600 °C and 400 °C.......... .....(8 points) Composition (at% Zn) 20 40 60 80 1200 100 2200 2000 a + L Liquid 1000 1800 B+L 1600 800 B 1400 2 Temperature (°C) Temperature (°F) 8 8 +L 1200 600 1000 7+ + Z у 400 800 8' TE B + 600 200 0 (Cu)...
14. Use the lead-tin phase diagram (below). A Sn-Pb alloy is heated to a temperature within the a liquid phase region. If the composition of the a phase is 10 wt% Sn, determine: a. The temperature of the alloy b. The composition of the liquid phase c. What is the maximum solubility of Sn in a and Pb in B? d. What is the eutectic composition for the Pb-Sn system? Composition (at% Sn) 0 20 40 60 80 100 327°C...