3. A [0/90]s graphite/epoxy laminate is subjected to a tensile normal load of 1N/m in the x- dire...
2. For a graphite/epoxy unidirectional lamina (un-oriented lamina), find the following: ,--3 MPa 1) Compliance matrix 2) Stiffness matrix 3) Resultant strain under the applied stresses 12-4 MP 2 MPa τ12 Typical Mechanical Properties of a Unidirectional Lamina (SI System of Units) Glass Boron/ Graphitel epoxy epoxy Property Symbol Units epoxy Fiber volume fraction Longitudinal elastic modulus E Transverse elastic modulus E, Major Poisson's ratio Shear modulus Ultimate longitudinal tensile (σ1he 0.45 0.70 10.30 7.17 GPa GPa 38.6 8.27 18.50...
235 Find the off-axis shear strength and mode of failure of a 60 boron/ epoxy lamina. Use the properties of a unidirectional boron/epoxy lamina from Table 2.1. Apply the maximum stress failure, maximum strain, Tsai-Hill, and Tsai-Wu failure theories. TABLE 2.1 Tvpical Mechanical Properties of a Unidirectional Lamina (SI System of Units) Glass Boron/ Graphite/ Property SymbolUnits epoxy epoxy epoxy Fiber volume fraction Longitudinal elastic modulus Transverse elastic modulus Major Poisson's ratio Shear modulus Ultimate longitudinal tensile strength Ultimate longitudinal...
6.1 A simply supported laminated composite beam (Figure
6.6) made of glass/epoxy is 75 mm long and has the layup of
[±30]2s. A uniform load is applied on the beam that is 5 mm in
width. Assume each ply is 0.125 mm thick and the properties of
glass/epoxy are from Table 2.1.
1. What is the maximum deflection of the
beam?
2. Find the local stresses at the top of the
laminate.
q- 100 N/m 0.075 m FIGURE 6.6 Uniformly...
homework help. need help figuring out out to solve this problem?
please show steps and box answer.
Find the local stresses at the middle of the 30° ply in a [30/45] glass/ epoxy laminate that is subjected to the following mechanical and hygrothermal loads: Nr 108 lb/in.; ΔΤ -100°F; AC 500. Use the properties of a unidirectional glass/epoxy lamina given in Table 2.2 The thickness of each lamina is 0.005 m TABLE 2.2 al Mechanical Properties of a Unidirectional Lamina...
please solve 2 and 3
1- The reduced stiffness matrix [Q] is given for a unidirectional lamina as follows: 5.681 0.3164 0 ] [Q]=0.3164 1.217 0 Msi I 0 0 0.6006 Calculate the four engineering constants E1, E2, V12, G12 of the lamina. 2- Calculate the transformed reduced stiffness [Q] for the above problem for 0 = 30°. Glass 3- A glass/epoxy lamina consists of 70% fiber volume fraction. Use properties of glass and epoxy from the tables below to...
Composite Structures Tutorial 7 (week 8) 7.1 Find the five strength parameters of a unidirectional glass/epoxy lamina with 40% fiber volume fraction. Use the properties of glass and epoxy from Table 3.1 and Table 3.2. Assume the fibers have circular cross-section and are in a square array packing. 1-52.0-$01674870 225 47 Find 208 Mechanics of Composite Materials, Second Edi Convert PO or Excel Orl Select PDF I TABLE 3.1 Typical Properties of Fibers (SI System of Units) Units Graphite Glass...
A 3 m rigid bar AB is supported with a vertical translational spring at A and a pin at B The bar is subjected to a linearly varying distributed load with maximum intensity g Calculate the vertical deformation of the spring if the spring constant is 700 kN/m. (ans: 21.43 mm) 2. A steel cable with a nominal diameter of 25 mm is used in a construction yard to lift a bridge section weighing 38 kN. The cable has an...