aluminum bar is subjected to repeated tension-compression cycling along 4. (10) A cylindrical 2014-T6 its axis (200 MPa stress) a) Will the bar fail from fatigue? b) if bar does fail, how many cyc...
A cylindrical 2014-T6 aluminum alloy bar is subjected to compression-tension stress cycling along its axis, results of these tests are shown in Animated Figure 8.20. If the bar diameter is 10 mm, calculate the maximum allowable load amplitude (in N) to ensure that fatigue failure will not occur at 1.0 x10' cycles. Assume a factor of safety of 2.9, data in Animated Figure 8.20 were taken for reversed axial tesion-compression tests, and that S is stress amplitude. FE N [The...
A 6.4 mm diameter cylindrical rod fabricated from a 2014-T6 aluminium alloy is subjected to reversed tension-compression load cycling along its axis of +7400 N to -2250N. Determine the fatigue life using the data shown below. 500 400 1045 steel 300 2014-T6 aluminum alloy 200 100 Red brass 10 103 104 106 105 108 10° 1010 Cycles to failure, N Stress amplitude, S (MPa) A 6.4 mm diameter cylindrical rod fabricated from a 2014-T6 aluminium alloy is subjected to reversed...
DUC. TUJU, NUVCHULI 20, 2013 Problem 8.18 A cylindrical 4340 steel bar is subjected to reversed rotating-bending stress cycling, which yielded the test results presented in Animated Figure 8.21. If the maximum applied load is 5,000 N, compute the minimum allowable bar diameter to ensure that fatigue failure will not occur. Assume a factor of safety of 2.25 and that the distance between loadbearing points is 55.0 mm. T-SAI-2.55n titanium alloy Maximum streSMP) 1045 steel Ductile cast iron 700 30...
A cylindrical bar of ductile cast iron is subjected to reversed and rotating-bending tests, test results (i.e., S-N behavior) are shown in Animated Figure 8.21. If the bar diameter is 8.52 mm, determine the maximum cyclic load that may be applied to ensure that fatigue failure will not occur. Assume a factor of safety of 2.21 and that the distance between loadbearing points is 55.3 mm. answer in N We were unable to transcribe this imageReferences Cycles to failure 3.2E...