position of 75% A and 25% B. The fill out the table indicating composition of ww.10...
Percent weight of material A 50 75 25 Melting temperature of material A Liquid Liquid and solid Melting temperature of material B Solid 0 25 50 Percent weight of material B 75 100 Consider an alloy of two soluble components A and B shown in the phase diagram. Determine the masses of the alloy that are in liquid and solid phases at a given temperature if the total mass of the alloy is 100 g, component B represents 60% of...
2. [25 points] The following figure shows the phase diagram of Cu-Ag alloy system. A mixture of Ag and Cu with a eutectic composition (or concentration) is heated to a high temperature and keep for enough time to prepare the material into a uniform liquid state. The material is then cooled down to 800°c. Cu-Ag System 1200 Liquid 800 A 600 400 100 80 60 40 20 wt% Ag a) What is the Ag composition in the original material so...
2. [20pt] Consider the temperature-composition phase diagram shown below, which represents a solid-liquid equilibrium based on a (liquid) mixture of A and B at high temperature. Temperature, T DY 0.16 0.23 0.57 0.67 0.84 0.2 0.8 0.4 0.6 Mole fraction of B, XE (a) Label all regions of the diagram according to the chemical species exist in that region and their phases. Be precise the composition of solid formed. (10pt) (b) Indicate the number of species and phases present at...
4. Use this melting-point-composition diagram for two substances, A and B, to answer the following questions : 120 100 + O nas 80 + + + mol % A mol 8 B + 100 0 + + + 80 - 60 40 200 20 40 60 80 100 Composition (mol ) A. What are the melting point and composition of the eutectic ? B. What is the theoretical melting temperature range for a mixture of 90 mol % A and...
3. On Silver-Copper phase diagram, label the liquidus line, eutectic point, and all unlabeled regions. Also answer questions below a. How many phases are there? b. What is the eutectic temperature? c. What is the eutectic concentration (in mass percent)? d. What is the composition of the Ag in the solid solution at the eutectic temperature? e. What is the composition of the Cu in the solid solution at the eutectic temperature? f. At 600°C what is the composition of...
2. [25 points] The following figure shows the phase diagram of Cu-Ag alloy syst em. A mixture of Ag and Cu with a eutectic composition (or concentration) is heated to a high temperature and keep for enough time to prepare the material into a uniform liquid state. The material is then cooled down to 800°C. Cu-Ag System 1200p Liquid 1000 800 A B. 600 400 200 100 80 60 40 20 wt% Ag (o) What is the Ag composition in...
Hypothetical phase diagram for A-B system is given below. A and B are both metals and atomic mass of B is much higher than that of A. ㄒ 421°C A 10.2 24.3 i) il in the boxes in the figure with proper phases. The following transformation reaction for the eutectic point for α and β phases is given; 1s3a123+B20.1 at 421°C iii) For an A-B mixture with a wt% of 18 at 420°C (alloy 1) and that with wt% of...
Can someone help with this material science problem? Problem 10.38 (GO Tutorial) For a copper-silver alloy of composition 24 wt% Ag-76 wt% Cu and at 775°C (1425°F) (see Animated Figure 10: (a) Determine the mass fractions of a and β phases Mass fraction a Mass fraction β- (b) Determine the mass fractions of primary a and eutectic microconstituents do the following: Mass fraction a primary Mass fraction eutectic (c) Determine the mass fraction of eutectic a Mass fraction a eutectic|...
Question 4 (25 marks) (a) Consider the hypothetical eutectic phase diagram for metal for lead-tin system. Assume that (1) A and B phase cutectic phase diagram for metals A and B, which is similar to that 1. Assume that (1) a and B phases exist at the A and B extremities of the phase diagram, respectively; (2) the eutectic composi m, respectively; (2) the eutectic composition is 36 wt% A-64 wt% B; and (3) the composition of the a phase...
6. Consider the Ti-Ni system in the figure below. Atomic Percent Nickel 20 I800 1600 L 1450C 1400 200 TIN (Ni) 1000 Un) re s00 Hati) s00 Ti Weight Percent Nickel N a. What are the melting temperatures of pure Ni and pure Ti? b. Label the liquidus and solidus lines in the figure. c. Label al field containing two phases in the figure. d. What is the maximum solubility of Ni in a-Ti and Ti in Ni? e. Write...