Nitrogen from a gaseous phase is to be diffused into pure iron at 700°C. If the surface concentration is maintained at 0.12 wt% N, what will be the concentration (in weight percent) 3.7 mm from the surface after 8.3 h? The diffusion coefficient for nitrogen in iron at 700°C is 3.0 × 10-10 m2/s.
Also, A cylindrical specimen of a brass alloy 10.1 mm (0.3976 in.) in diameter and 119.8 mm (4.717 in.) long is pulled in tension with a force of 12000 N (2698 lbf); the force is subsequently released. The tensile stress-strain behavior for this alloy is shown in the Animated Figure 6.12. Compute the final length of the specimen at this time. answer in milimeters
Nitrogen from a gaseous phase is to be diffused into pure iron at 700°C. If the...
Nitrogen from a gaseous phase is to be diffused into pure iron at 700°C. If the surface concentration is maintained at 0.12 wt% N, what will be the concentration (in weight percent) 3.9 mm from the surface after 6.5 h? The diffusion coefficient for nitrogen in iron at 700°C is 4.1 x 10-10 m²/s. 1.7 z erf(z) 0.00 0.0000 0.025 0.0282 0.05 0.0564 0.10 0.1125 0.15 0.1680 0.20 0.2227 0.25 0.2763 0.30 0.3286 0.35 0.3794 0.40 0.4284 0.45 0.4755 0.50...
UTVER VIS Concentration of Nitrogen (wt%): = 0.21 Position in mm= 7.2 Diffusion Coefficient for Nitrogen in Iron at 700°C -8.90E-10 Nitrogen in Iron Heat Treatment Time (hours): = 8 Carburizing Time (hrs): = 7 Steel Alloy Case Depth (mm): 4.8 Steel Alloy New Case Depth (mm) - 9.9 Activation Energy kJ/mol: = 103 Temperature for Problem 3 (Celsius) -809 . Data for Problem 4 Temperature in C: -595 Diffusivity (m2/s) = 5.62E-14 Temperature in C: -702 Diffusivity (m /s)...
Niobium forms a substitutional solid solution with vanadium. Compute the weight percent of niobium that must be added to vanadium to yield an alloy that contains 1.55 times 10%22 Nb atoms per cubic centimeter. The densities of pure Nb and V are 8.57 and 6.10 g/cm^3, respectively. Gold forms a substitutional solid solution with silver. Compute the number of gold atoms per cubic centimeter for a silver-gold alloy that contains 10 wt% Au and 90 wt% Ag. The densities of...