An experiment was performed to compare the fracture toughness of high-purity 16 Ni maraging steel with commercial purity steel of the same type Form 30 specimens, the sample average toughness was x = 65.4 for the high-purity steel, whereas for n - 39 specimens of commercial steel y = 59.9. Because the high-punity to is more expensive, its use for a certain application can be justified only if its fracture toughness exceeds that of commercial purity steel by more than...
An experiment was performed to compare the fracture toughness of high-purity 18 Ni maraging steel with commercial-purity steel of the same type. For m = 32 specimens, the sample average toughness was x = 64.3 for the high-purity steel, whereas for n = 37 specimens of commercial steel y = 58.8. Because the high-purity steel is more expensive, its use for a certain application can be justified only if its fracture toughness exceeds that of commercial-purity steel by more than...
An experiment was performed to compare the fracture toughness of high-purity 18 Ni maraging steel with commercial-purity steel of the same type. For m = 31 specimens, the sample average toughness was x = 65.3 for the high-purity steel, whereas for n = 38 specimens of commercial steel y = 59.5. Because the high-purity steel is more expensive, its use for a certain application can be justified only if its fracture toughness exceeds that of commercial-purity steel by more than...
Will give instant thumbs up, please show some work and equations if done in excel. An experiment was performed to compare the fracture toughness of high-purity 18 Ni maraging steel with commercial-purity steel of the same type. For m = 33 specimens, the sample average toughness was x = 64.1 for the high-purity steel, whereas for n = 38 specimens of commercial steel y = 58.6. Because the high-purity steel is more expensive, its use for a certain application can...
question b An experiment was performed to compare the fracture toughness of high-purity 18 Ni maraging weel with commercial purity of the for average toughness was 65.4 for the high-purity steel, whereas for - 39 specimens of commercially-59.9. Because the certain application can be justified only if its fracture toughness exceeds that of commercial purity Weel by more than 5. Suppose that the (a) Assuming that - 1.4 anda, - 1.0, test the relevant hypotheses using a 0.001.( UM), where...
An experiment was performed to compare the fracture toughness of high-purity 18 Ni maraging steel with commercial-purity steel of the same type. For m = 34 specimens, the sample average toughness was x = 64.2 for the high-purity steel, whereas for n = 39 specimens of commercial steel y = 58.5. Because the high-purity steel is more expensive, its use for a certain application can be justified only if its fracture toughness exceeds that of commercial-purity steel by more than...
An experiment was performed to compare the fracture toughness of high-purity 18 Ni maraging steel with commercial-purity steel of the same type. For m = 30 specimens, the sample average toughness was x = 65.5 for the high-purity steel, whereas for n = 39 specimens of commercial steel y = 59.9. Because the high-purity steel is more expensive, its use for a certain application can be justified only if its fracture toughness exceeds that of commercial-purity steel by more than...
An experiment was performed to compare the fracture toughness of high-purity 18 Ni maraging steel with commercial-purity steel of the same type. Form 34 specimens, the sample average toughness was x = 63.1 for the high-purity steel, whereas for n = 39 specimens of commercial steel y = 57.3. Because the high- purity steel is more expensive, its use for a certain application can be justified only if its fracture toughness exceeds that of commercial-purity steel by more than 5....
An experiment was performed to compare the fracture toughness of high-purity 18 Ni maraging steel with commercial purity steel of the same type. For m = 34 specimens, the sample average toughness was x = 63.1 for the high-purity steel, whereas for n = 39 specimens of commercial steel y = 57.3. Because the high- purity steel is more expensive, its use for a certain application can be justified only if its fracture toughness exceeds that of commercial-purity steel by...
An experiment was performed to compare the fracture toughness of high-purity 18 Ni maraging steel with commercial purity steel of the same type. For m = 34 specimens, the sample average toughness was x = 63.1 for the high-purity steel, whereas for n = 39 specimens of commercial steel y = 57.3. Because the high- purity steel is more expensive, its use for a certain application can be justified only if its fracture toughness exceeds that of commercial-purity steel by...