Find the degree of polymerization for polyethylene with an number average molecular weight of 500,000 g/mol
Find the degree of polymerization for polyethylene with an number average molecular weight of 500,000 g/mol
Find the degree of polymerization for polyethylene with an number average molecular weight of 500,000 g/mol.
Find the degree of polymerization for polyethylene with an number average molecular weight of 500,000 g/mol
this is the full table Problem 5 (10pts) The following table lists molecular weight data for a polyethylene material. Compute (a) the number-average molecular weight, and (b) the degree of polymerization. Molecular Weight Range (g/mol) 8,000-20,000 20,000-32,000 32,000-44,000 44,000-56,000 56,000-68,000 68,000-80,000 80,000-92,000 Problem 5 (10pts) The following table lists molecular weight data for a polyethylene material. Compute (a) the number-average molecular weight, and (b) the degree of polymerization. Molecular Weight Range (g/mol) 8,000-20,000 20,000-32,000 32,000-44,000 44,000-56,000 56,000-68,000 68,000-80,000 80,000-92,000
(1 point) Determine the degree of polymerization of polypropylene with a number-average molecular weight of 845000 g/mol Degree of polymerization =
An alternating copolymer is known to have a number-average molecular weight of 250,000 g/mol and a number-average degree of polymerization of 3406. One of the alternating mers is polystyrene which has a molecular weight of 105_g/mol. Given that the molecular weight of polypropylene is 42 g/mol and that of polyvinyl chloride is 61.5 g/mol, Which of them is the other alternating mer?
7. (19 points) The number average molecular weight of polypropylene is 1,5 Calculate the degree of polymerization. 00,000 g/mol.
Incorrect The tensile strength and number-average molecular weight for two polyethylene materials are as follows: Tensile Strength (MPa) Number-Average Molecular Weight (g/mol) 20,000 40,000 190 Estimate the number-average molecular weight that is required to give a tensile strength of 79 MPa. g/mol
It is desired to prepare polyester with the number average molecular weight, Mn 5000 g/mol by reacting of 1 mol butane-1,4 diol (HO-CH-CH2-CH2-CH2-OH) with 1 mol of adipic acid (HOOC-CH2-CH2-CH2-CH2-COOH) (a) Write chemical equation illustrating synthesis of the polyester. (b) Calculate the value of the monomer conversion at which the reaction should be stopped to obtain this polymer, assuming perfect stoichiometric balance. What would be polydispersity index for the polymer obtained? (c) Assuming that 0.5 mol % of the diol...
4 (20 Points) Calculate the number-average molecular weight and the weight average molecular weight of a polymer sample made of polystyrene with a repeat unit of (CH2- CH(CHs)) and composed of two types of chains. 60 percent of the chains have a degree of polymerization of 7,000 and the rest 50,000. Carbon has an atomic weight of 12 g/mol and hydrogen is 1 g/mol.
The monomer seen below is called ethylene. Through addition polymerization it can be made into polyethylene, which goes by the abbreviation PE. Determine the degree of polymerization (DP) of a PE polymer with a molecular weight of 158900 g/mol Number DP- 1589