Determine the polydispersity index for polystyrene having the following molecular weight distributions:
The polydispersity index is the ratio of Molecular weight averages.
Polydispersity Index (PDI ) = Mw / Mn
PDI = ( 5000 + 7000 + 9000 + 11000 + 13000) / ( 2+15+17+12+4)
= 45000 / 50
= 900
Answer ; (PDI ) = 900
Determine the polydispersity index for polystyrene having the following molecular weight distributions:
a) compute the repeat unit molecular weight of polystyrene b) compute the number-average molecular weight for polystyrene for which the degree of polymerization is 26,000. 54 (a) Compute the repeat unit molecular weight of polystyrene. (b) Compute the number-average molecular weight for a polystyrene for which the degree of polymerization is 26,000.
Compute the repeat unit molecular weight of polystyrene. (b) Compute the number-average molecular weight for a polystyrene for which the degree of polymerization is 25,000. Please write legibly Please handwrite.
Polystyrene can be polymerized from the starting monomer (styrene) pictured below. a. Anionic polymerization is one method of polymerization that can be used to generate polystyrene from styrene. Explain what type of initiator should be used for this reaction and draw an example of a styrene monomer that has reacted with initiator. b. Using this anionic polymerization method and a starting concentration of 1M styrene and 1mM initiator, what degree of polymerization (Xn) would you expect if you use up...
What would be the number-average molecular weight of polystyrene obtained at the completion of an anionic (i.e., “living”) polymerization in which 0.01 g of n-butyllithium and 10 g of styrene monomer are used? The molecular weight of butyllithium and styrene are 64.06 and 104.12, respectively.
Please show detailed calculations. Thanks in advance! Question 2: Calculate Mn. Mw and polydispersity index of 2 equally weight polystyrene of 1000 g/mol and 10000 g/mol.
14. (a) Compute the repeat unit molecular weight of polystyrene and the number-average (b) Viscoelastic creep of some polymer materials can be modelled using a spring and dashpot molecular weight of the material if the degree of polymerisation is 25,000. in parallel configuration as shown in the following figure. Derive the mathematical expression for the strain as a function of time. 凹η (6+6 marks
polymer question A polystyrene sample is made by mixing two types of polystyrene chains. The weight fractions of each type are the same. The degree of polymerization of the first chain type is 96, for the second is 192. What is the number average molecular weight of this mixture?
1. A sample of polystyrene has a number average molecular weight of 30,000 daltons. What is the number average degree of polymerization (n)? The mer structure is shown below, amu are C-12, H-1; 1 dalton 6.023x103 grams
Three batches of polystyrene are synthesized separately and combined without further reaction. A) Given the information in the table below, calculate Mn and Mw for the mixture B) Based on polydispersity index, what type of polymerization method was most likely #used to produce batch A, B and C Batch Weight in Mixture Mn(g/mol) Mw (g/mol) B 20 75 5 500000 250000 10000 500000 375000 60000
1 Polymer Structure (4 pts) Sketch the repeat unit and determine the repeat unit molecular weight for the following polymers: a. polystyrene b. polytetrafluoroethylene c. polydimethylsiloxane d. nylon 6,10