· A) r=()=()=0,293
B) =ln= =0,348
Yf===271Mpa
D===2,3
Lc===0,647mm
=0,88+0,12()=1,3
d=Yf(1+()ln = d=271(1+()1,3*ln=153 MPa
C) f=Af* d=3,46*153=528,64N
· A) r=()=()=0,293
B) =ln= =0,348
Yf===271Mpa
D===2,3
Lc===0,647mm
=0,88+0,12()=1,3
d=Yf(1+()ln = d=271(1+()1,3*ln=153 MPa
C) f=Af* d=3,46*153=528,64N
5. A spool of Cu wire has a starting diam. Of 2.5 mm. It is drawn...
Q7) Bar stock of initial diameter = 90 mm is drawn with a draft = 15 mm. The draw die has an entrance angle 18, and the coefficient of friction at the work-die interface 0.08. The metal behaves as a perfectly plastic material with yield stress 105 MPa. Determine (a) area reduction, (b) draw stress, (c) draw force required for the operation, and (d) power to perform the operation if exit velocity-1.0 m/min Q7) Bar stock of initial diameter =...
A rod is drawn from a diameter of 43.0 mm to a diameter of 21.1 mm in a draw die of 19.2°. The coefficient of friction is 0.120. Take the strength coefficient (K) as 321 MPa and the strain- hardening exponent as 0.258. a) Expected answer: 14238541504 Determine the true strain. b) Expected answer: 280 MPa Determine the average flow stress (of) c) Determine the ideal drawing force when friction is negligible. Use the ideal, no friction drawing stress formula....
A cylindrical part has a diameter – 2.5 in and a height = 4 in it is upset forged to a height 2.75 in a coefficient of friction at the die work interface = .10 the work material has a flow curve with strength coefficient= 25000 lb/in and strain hardening exponent = .22 compute the forging force F at the following values of part height a) h = 4.0 in ? b)h=2.75 in ?
zis 3. A Cylindrical billet is 75 mm long and 35 mm in diameter. It is reduced by direct extrusion to 20 mm diameter. The half die angle x 45°. In the flow curve for the work metal, strength coefficient 500 MPa and strain-hardening exponent -0.25, Coefficient of friction at the work- die interface 0.15. Given that total extrusion pressure P, is the sum of the die pressure P and the friction pressure P, between the container and the extruded...
Given: the steel has a strength coefficient of 530 MPa, a strain hardening coefficient of 0.26, elastic modulus 200 GPa. The drawing process has a friction coefficient of 0.15, a die angle (2α =12 deg), and no redundant work. (a) What is the maximum reduction that can be achieved in a single pass? (b) Find the force needed to draw the wire through a second die that also provides 30% reduction (also with friction coefficient of 0.15, 2α =12 deg),...
(15 pts) 6. A cylindrical part is forged in an open die. The starting diameter = 50 mm and height = 40 mm. Height after forging = 30 mm. Coefficient of friction at the die-work interface = 0.20. Yield strength of the low-carbon steel work material = 105 MPa; its strength coefficient = 500 MPa and strain hardening exponent = 0.25. Determine (a) the romarse force for the viviu point is reacha ... tegenkor Lici........ .he longer tha n (a)...
Assignment 01 TOT Mechanical Properties of Materials 1. A tensile test specimen has a gage length = 50 mm and its cross-sectional area = 100 mm. The specimen yields at 48,000 N, and the corresponding gage length - 50.23 mm. This is the 0.2 ent yield point. The maximum load of 87,000 N is reached at a gage length 64.2 mm. Determine (a) yield strength, (b) modulus of elasticity, and (c) tensile strength. (d) If fracture occurs at a gage...
Q.6 Rolling A 28+Y mm thick, 275+X mm wide metal strip is fed through a two – high rolling mill; each roll has a radius of 240+Z mm having a rotational speed of 48+Z rpm. The strip thickness is to be reduced to 24+Y mm in one pass. The strength coefficient of the work material is 270 MPa and strain-hardening exponent is 0.12. Determine: a- The minimum coefficient of friction between the strip and roll surface μ (Use dmax =...