From the copper-nickel phase diagram determine the approximate temperature, composition, phases for the point labeled B.
Group of answer choices
a. 1250 C, 35 wt % Cu, solid alpha + liquid
b. 1453 C, 35 wt % Ni, solid alpha
c. 1085 C, 35 wt % Ni, liquid
d. None of the answers is correct.
e. 1250 C, 35 wt % Ni, solid alpha + liquid
Option e is correct. at 1250 degree C , we have solid alpha and liquid ( 35 % Ni and 65 % Cu)
From the copper-nickel phase diagram determine the approximate temperature, composition, phases for the point labeled B....
A copper-nickel alloy of composition (40% Ni-60% Cu) is slowly heated from a temperature of 1200°C: 1. a) At what temperature does the first liquid phase form? b) What is the composition of this liquid phase? c) At what temperature does complete melting of the alloy occur? d) What is the composition of the last solid remaining prior to complete melting? Composition (at% N) 100 0 1600 2800 1500 1453°C Liquid 2600 Soldus line Liquidus line 1300 - 2200 120아ㅡㅡㅡㅡㅡ...
A Cu-Ni alloy is slowly cooled to 1250°C. Both liquid and solid coexist. If the amount of liquid is 26%, determine the overall composition of the alloy (in wt% Ni). Composition (at% Ni) 0 20 40 1600 TTT 60 80 100 2800 1500 Liquid 1453°C 2600 1400 Liquidus line Solidus line Temperature (°C) 00 Temperature (°F) 1200 2200 1100 2000 1085°C 1000 LL 0 20 80 100 40 60 Composition (wt% Ni) (Cu) (Ni)
3. On Silver-Copper phase diagram, label the liquidus line, eutectic point, and all unlabeled regions. Also answer questions below a. How many phases are there? b. What is the eutectic temperature? c. What is the eutectic concentration (in mass percent)? d. What is the composition of the Ag in the solid solution at the eutectic temperature? e. What is the composition of the Cu in the solid solution at the eutectic temperature? f. At 600°C what is the composition of...
Due date: April 7, 2020 200 Solubaty limit- Homework #7 (Chapter 9: Phase Diagrams) 150 Liquid solution Ganes Solution sugar 100 1 50 1. Consider the Cu-Ni binary Liquid solution (syrup) phase diagram (see the following old figure) and answer the questions: A copper-nickel alloy of composition 70 wt% Ni-30 wt% 207 Cu is slowly heated from a temperature of 1300°C. Il (a) At what temperature does the Sugar 60 80 Water 100 first liquid phase form? (b) What is...
4. A composite of Aluminum and Nickel is composed of 50 wt. % Ni. The phase diagram of Al and Ni is shown below. Find the following at 500 °C (2.5 point) a) What phase or phases we have at 50 wt. % Ni. b) If your answer to part (a) is one phase, what is the amount and composition of that phase. If your answer to part (a) consists of two phases, determine the amount of each phase and...
Consider the Cu-Ag phase diagram provided. What phases are present at equilibrium if an alloy of Cu-50wt%Ag is held at 800°C. What are the compositions of the phases? Composition (at% Ag) - 40 60 80 1200 2200 100 2000 -Liquidus Liquid -Solidus ar + L 800 779°C (Te) 71.9 Temperature (°C) 91.2 (CBE) Temperature (°F) Solvus + B 20 80 100 40 60 Composition (wt% Ag) (Cu) (Ag) The phases present are a (8 wt%Ag, 92 wt%Cu) and B (93...
In the Al-Cu phase diagram, determine what phases are present in the binary areas (white area). Determine all the phase transformations happened in the following phase diagram. For a 20 wt% Cu alloy at 500 oC, determine: The phases present The phase compositions The fraction of each phase Draw microstructure of this alloy at 700 oC, 560 oC and 300 oC. We are interested to design an alloy with heat treatable characteristics. Please suggest a composition range and explain why?...
6. Consider the Ti-Ni system in the figure below. Atomic Percent Nickel 20 I800 1600 L 1450C 1400 200 TIN (Ni) 1000 Un) re s00 Hati) s00 Ti Weight Percent Nickel N a. What are the melting temperatures of pure Ni and pure Ti? b. Label the liquidus and solidus lines in the figure. c. Label al field containing two phases in the figure. d. What is the maximum solubility of Ni in a-Ti and Ti in Ni? e. Write...
1. From the phase diagram for a binary mixture of titanium and nickel, find: a. label the two-phase regions with the phases present in each case. b. The phase or phases present in a mixture of 2g nickel with 48g titanium @ 1000C c. Amount of additional nickel in g required for the alloy to start to form a liquid at 1000C. d. Composition of the first liquid that starts to form as nickel is added to this alloy e....
2. [25 points] The following figure shows the phase diagram of Cu-Ag alloy system. A mixture of Ag and Cu with a eutectic composition (or concentration) is heated to a high temperature and keep for enough time to prepare the material into a uniform liquid state. The material is then cooled down to 800°c. Cu-Ag System 1200 Liquid 800 A 600 400 100 80 60 40 20 wt% Ag a) What is the Ag composition in the original material so...