A specimen is originally 1 ft long, has a dimeter of 0.5 in, and is subjected to a force of 500 lb. When the force is increased from 500 lib to 1800 lb, the specimen elongates 0.009 inch. Determine the modulus of elasticity if it remains in the linear elastic region. If the Poisson’s ratio is .33, determine lateral strain and reduction in diameter.
It's a simple problem hope you will understand it easily if you find it helpful please rate it positive or else if anything went wrong with this problem please leave a comment below so that I will respond as soon as possible.
Thank you
Have a great day.
A specimen is originally 1 ft long, has a dimeter of 0.5 in, and is subjected...
Due to the operational conditions and temperature gradient, a 95 mm diameter, 1.75 m long steel rod within a machine assembly is subjected to a combination of tensile loading of 190 N and thermal loading which imposes a longitudinal force of 244 N. The total loading results in an even distribution of forces on the body of the rod causing it to change its dimensions by increasing 0.45 mm in length at both ends and decreasing by 0.0135 mm at...
Due to the operational conditions and temperature gradient, a 95 mm diameter, 1.75 m long steel rod within a machine assembly is subjected to a combination of tensile loading of 190 N and thermal loading which imposes a longitudinal force of 244 N. The total loading results in an even distribution of forces on the body of the rod causing it to change its dimensions by increasing 0.45 mm in length at both ends and decreasing by 0.0135 mm at...
6 6.19 Consider a cylindrical specimen of some hypothetical metal alloy that has a diameter of 8.0 mm (0.31 in), A tensile force of 1000 N (225 lb) produces an elastic reduction in diameter of 2.8 x 101mm (1.10 x10 in,). Compute the modulus of elasticity for shis alloy, given that Poisson's ratio is 0.30
Assignment 01 TOT Mechanical Properties of Materials 1. A tensile test specimen has a gage length = 50 mm and its cross-sectional area = 100 mm. The specimen yields at 48,000 N, and the corresponding gage length - 50.23 mm. This is the 0.2 ent yield point. The maximum load of 87,000 N is reached at a gage length 64.2 mm. Determine (a) yield strength, (b) modulus of elasticity, and (c) tensile strength. (d) If fracture occurs at a gage...
(a) A wood bar is subjected to tensile force of 60 kips at two ends. It is 5 ft long, and has the rectangular Cross section which height is 4 in, and width is 2 in. The modulus of elasticity is 1.9×103ksi. Determine the total clastic deformation of the wood bar. Answer in the unit of inches, to 0.001. Note: 1 ft = 12 in., 1 ksi = 1000 psi. (b) If this wood bar has a hole with a diameter...
Problem #1 A cylindrical rod of copper (E 110 GPa) having a yield strength of 240 MPa is to be subjected to a load of 6660 N. If the length of the rod is 380 mm, what must the diameter be to allow an elongation of 0.50 mm? A cylindrical specimen of some alloy 8 mm in diameter is stressed elastically in tension. A force of 15,700 N produces a reduction in the specimen diameter of 5 10-3 mm. Compute...
Part B Calculate the load II Review A square steel bar has a length of 2.2 ft and a 1.5 in by 1.5 in cross section and is subjected to axial compression. Under load, the thickness becomes 1.50032 in . If the modulus of elasticity is E = 2.9x 104 ksi and Poisson's ratio is v = 0.31; what is the magnitude of the load that was applied to the bar? Learning Goal To use Poisson's ratio and Hooke's law...
i only need help with Q3
CEE 216 Civil Engineering Materials Steel 1. A 32-mm rebar with a gauge length of 200 mm was subjected to tension to fracture according to ASTM E-8 method. The load and deformation data collected are shown in Table 1. Create a spreadsheet to complete the following. Table 1. Load and displacement data for a 32-mm rebar sample subjected to an increasing tensile load a. Create a plot of stress-strain. Label the axes and show...