Add Answer to:
An uncold-worked brass specimen of average grain size 0.008 mm has a yield strength of 163...
An uncold-worked brass specimen of average grain size 0.008 mm has a yield strength of 151...
An uncold-worked brass specimen of average grain size 0.008 mm has a yield strength of 151 MPa. Estimate the yield strength of this alloy (in MPa) after it has been heated to 600°C for 1220 s, if it is known that the value of ky is 11.5 MPa-mm 1/2. The Animated Figure 7.25 may be helpful. MPa (The tolerance is +/- 10%.) Click if you would like to Show Work for this question: Open Show Work
The yield strength for an alloy that has an average grain diameter of 5.7 × 10-2...
The yield strength for an alloy that has an average grain
diameter of 5.7 × 10-2 mm is 140 MPa. At a
grain diameter of 7.3 × 10-3 mm, the yield
strength increases to 277 MPa. At what grain diameter, in mm, will
the yield strength be 228 MPa?
d =
mm
We were unable to transcribe this imageThe yield strength for an alloy that has an average grain diameter of 5.7 x 10-2 mm is 140 MPa. At a...
The yield strength for an alloy that was an average grain diameter of 5.4 x 102...
The yield strength for an alloy that was an average grain diameter of 5.4 x 102 mm is 133 MPa. At a grain diameter of 7.4 x 10 mm, the yield strength increases to 250 MPa. At wh grain diameter, in mm, will the yield strength be 203 MPa? mm the tolerance is +/-6% Click if you would like to Show Work for this question: Open Show Work
A brass alloy is known to have a yield strength of 275 MPa (40,000 psi), a...
A brass alloy is known to have a yield strength of 275 MPa (40,000 psi), a tensile strength of 380 MPa (55,000 psi), and an elastic modulus of 103 GPa (15.0×106 psi). A cylindrical specimen of this alloy 9.0 mm (0.35 in.) in diameter and 245 mm (9.65 in.) long is stressed in tension and found to elongate 9.0 mm (0.35 in.). A) What is the yield strain? B) What is the test strain?
S. (2 Marks) An alloy with an average grain diameter of 35 um has a yield...
S. (2 Marks) An alloy with an average grain diameter of 35 um has a yield strength of 163 Mpa. and when it undergoes strain hardening, the grain diameter reduces to 17 um with an increase in yield strength to 192 MPa. If the coarseness of the alloy desired for a particular application cannot exceed 12 um, what will be the expected yield strength?
A cylindrical specimen of a cold-worked brass has a ductility (%EL) of 33%. If its cold-worked...
A cylindrical specimen of a cold-worked brass has a ductility
(%EL) of 33%. If its cold-worked radius is 11 mm, what was its
radius before deformation? You may need to use Animated Figure
7.19c.
Percent cold work = 0 Ductility = 0 Ductility (%EL) Brass 1040 Steel Copper 10 60 70 20 30 40 50 Percent cold work
Problem 7.23 Your answer is partially correct. Try again. Consider the brass alloy for which the ...
Can someone help me with this materials problem?
Problem 7.23 Your answer is partially correct. Try again. Consider the brass alloy for which the stress-strain behavior is shown in the Animated Figure 7.12. A cylindrical specimen of this material 10.1 mm (0.3976 in.) in diameter and 98.8 mm (3.890 in.) long is pulled in tension with a force of 10200 N (2293 lbr). If it ls known that this alloy has a value for Polsson's ratio of 0.35, compute (a)...
Question 4: A cylindrical specimen of cold-worked copper has a ductility (%EL) of 25% What is its tensile strength? (a...
Question 4: A cylindrical specimen of cold-worked copper has a ductility (%EL) of 25% What is its tensile strength? (a) (b) If its cold-worked radius is 10 mm, what was its radius before deformation? 70 140 120 900 800 1040 Steel 60 120 1040 Stee 800 700 100 50 700 600 100 80 40 600 500 Brass Brass 80 30 60 400 500 Brass 20 Copper 40 300 60 400 Copper 10 1040 Stee 200 300 40 20 Copper 100...
An uncold-worked brass specimen of average grain size 0.008 mm has a yield strength of 151 MPa. Estimate the yield strength of this alloy (in MPa) after it has been heated to 600°C for 1220 s, if it is known that the value of ky is 11.5 MPa-mm 1/2. The Animated Figure 7.25 may be helpful. MPa (The tolerance is +/- 10%.) Click if you would like to Show Work for this question: Open Show Work
The yield strength for an alloy that has an average grain
diameter of 5.7 × 10-2 mm is 140 MPa. At a
grain diameter of 7.3 × 10-3 mm, the yield
strength increases to 277 MPa. At what grain diameter, in mm, will
the yield strength be 228 MPa?
d =
mm
We were unable to transcribe this imageThe yield strength for an alloy that has an average grain diameter of 5.7 x 10-2 mm is 140 MPa. At a...
The yield strength for an alloy that was an average grain diameter of 5.4 x 102 mm is 133 MPa. At a grain diameter of 7.4 x 10 mm, the yield strength increases to 250 MPa. At wh grain diameter, in mm, will the yield strength be 203 MPa? mm the tolerance is +/-6% Click if you would like to Show Work for this question: Open Show Work
S. (2 Marks) An alloy with an average grain diameter of 35 um has a yield strength of 163 Mpa. and when it undergoes strain hardening, the grain diameter reduces to 17 um with an increase in yield strength to 192 MPa. If the coarseness of the alloy desired for a particular application cannot exceed 12 um, what will be the expected yield strength?
A cylindrical specimen of a cold-worked brass has a ductility
(%EL) of 33%. If its cold-worked radius is 11 mm, what was its
radius before deformation? You may need to use Animated Figure
7.19c.
Percent cold work = 0 Ductility = 0 Ductility (%EL) Brass 1040 Steel Copper 10 60 70 20 30 40 50 Percent cold work
Can someone help me with this materials problem?
Problem 7.23 Your answer is partially correct. Try again. Consider the brass alloy for which the stress-strain behavior is shown in the Animated Figure 7.12. A cylindrical specimen of this material 10.1 mm (0.3976 in.) in diameter and 98.8 mm (3.890 in.) long is pulled in tension with a force of 10200 N (2293 lbr). If it ls known that this alloy has a value for Polsson's ratio of 0.35, compute (a)...
Question 4: A cylindrical specimen of cold-worked copper has a ductility (%EL) of 25% What is its tensile strength? (a) (b) If its cold-worked radius is 10 mm, what was its radius before deformation? 70 140 120 900 800 1040 Steel 60 120 1040 Stee 800 700 100 50 700 600 100 80 40 600 500 Brass Brass 80 30 60 400 500 Brass 20 Copper 40 300 60 400 Copper 10 1040 Stee 200 300 40 20 Copper 100...
Most questions answered within 3 hours.
-
Derive ground state term symbols. Use notation 2S(1/2) for state
2S1/2
a) d5
b) f3
c)...
asked 12 minutes ago -
A sample of size 31 will be drawn from a population with mean 39
and standard...
asked 51 minutes ago -
What is the effect on the P-value when a test is changed from a
two-tailed hypothesis...
asked 56 minutes ago -
I wish to estimate µ, the mean of a population. After I collect
and an-
alyze...
asked 1 hour ago -
At a local university, you poll a group of 115 students and find
that 37 of...
asked 1 hour ago -
Gladstone company tracks the number of units purchased and sold
throughout each accounting period but applies...
asked 1 hour ago -
When determining if a molecule's configuration is E or Z, what
determines the higher priority groups?
asked 1 hour ago -
13. What is the amount
of conversion cost transferred to finished goods? (Round
your intermediate calculations...
asked 1 hour ago -
Sulfuric Acid is a "strong" acid, but only releases a single
proton when it dissolves. What...
asked 1 hour ago -
The
second floor of a house is 6 m above the street level. How much
work...
asked 1 hour ago -
What uncontrollable factor(s) contributed to Hong Kong Disney’s
poor performance during its first year?
asked 1 hour ago -
You are interested in whether students that have a male
instructors perform differently on exams. To...
asked 1 hour ago