For an alloy that consists of 90.2 g copper, 104.5 g zinc, and 2.7 g lead,...
For an alloy that consists of 96.0 g copper, 102.2 g zinc, and 8.9 g lead, what are the concentrations of (a) Cu, (b) Zn, and (c) Pb in weight percent? The atomic weights of Cu, Zn, and Pb are 63.54, 65.39, and 207.2 g/mol, respectively.
For an alloy that consists of 95.6 g copper, 101 g zinc, and 7.43 g lead, what are the concentrations (a) of Cu (in at%), (b) of Zn (in at%), and (c) of Pb (in at%)? The atomic weights for Cu, Zn, and Pb are 63.55, 65.39, and 207.2 g/mol, respectively. (a) Enter your answer for part (a) in accordance to the question statement at% (b) Enter your answer for part (b) in accordance to the question statement at% (c)...
question 1 Calculate the fraction of atom sites that are vacant for silver at 650°C. Assume an energy for vacancy formation of 0.63 eV/atom. question 2 Calculate the number of vacancies per cubic meter in some metal at 663°C. The energy for vacancy formation is 0.71 eV/atom, while the density and atomic weight for this metal are 6.25 g/cm3 (at 663°C) and 86.84 g/mol, respectively. m-3 question 3 For an alloy that consists of 76.9 g copper, 118 g zinc,...
A materials scientist has created an alloy containing aluminum, copper, and zinc, and wants to determine the percent composition of the alloy. The scientist takes a 12.502 g sample of the alloy and reacts it with concentrated HCI. The reaction converts all of the aluminum and zinc in the alloy to aluminum chloride and zinc chloride in addition to producing hydrogen gas. The copper does not react with the HCI. Upon completion of the reaction, a total of 9.78 L...
Answer the following questions with regard to an alloy of copper with 64 percent of lead that is slowly cooled in a crucible without being stirred from 1100C to room temperature (a) What is the nature of the alloy at 1100 C? (b) Now consider the alloy at a temperature just above the monotectic temperature at 955C, where it is composed of the two liquids of different compositions. Do the liquids have the same density? If not, what would you...
A materials scientist has created an alloy containing aluminum, copper, and zinc, and wants to determine the percent composition of the alloy. The scientist takes a 11.282 g sample of the alloy and reacts it with concentrated HCl. The reaction converts all of the aluminum and zinc in the alloy to aluminum chloride and zinc chloride in addition to producing hydrogen gas. The copper does not react with the HCl. Upon completion of the reaction, a total of 8.70 L...
Question 2 What is the composition, in atom percent of an alloy that consists of 4.5 wtPb and 95.5 wt% Sn? The atomic weights for Pb and Snare 207.19 g/mol and 118.71 g/mol, respectively a. 2.6 Pb and 97.4 % Sn Ob 7.6 % Pb and 92.4 ats 97.4 at Ph and 2.65 Od 92.4 at Ph and 7.6 at% Sn
A 0.4505 g sample of pewter, containing tin, lead, copper, and zinc, was dissolved in acid. Tin was precipitated as SnO2⋅4H2Oand removed by filtration. The resulting filtrate and washings were diluted to a total volume of 250.0 mL. A 15.00 mL aliquot of this solution was buffered, and titration of the lead, copper, and zinc in solution required 35.10 mL of 0.001497 M EDTA. Thiosulfate was used to mask the copper in a second 20.00 mL aliquot. Titration of the...
1. A 0.7336-g sample of an alloy containing copper and zinc is dissolved in 8 M HCl and diluted to 100 mL in a volumetric flask. In one analysis, the zinc in a 25.00-mL portion of the solution is precipitated as ZnNH4PO4, and subsequently isolated as Zn2P2O7, yielding 0.1163 g. The copper in a separate 25.00-mL portion of the solution is treated to precipitate CuSCN, yielding 0.1931 g. Calculate the %w/w Zn and the %w/w Cu in the sample.
Question 2 of 5 A 0.4686 g sample of pewter, containing tin, lead, copper, and zinc, was dissolved in acid. Tin was precipitated as Sno, .4H, O and removed by filtration. The resulting filtrate and washings were diluted to a total volume of 200.0 mL. A 20.00 mL aliquot of this solution was buffered, and titration of the lead, copper, and zinc in solution required 35.16 mL of 0.001543 M EDTA. Thiosulfate was used to mask the copper in a...