1. A large plate is fabricated from a steel alloy that has a plane strain fracture toughness of 8...
A large plate is fabricated from a steel alloy that has a plane strain fracture toughness...
A large plate is fabricated from a steel alloy that has a plane strain fracture toughness of 75 MPam (68.25 ksi vin.). If the plate is exposed to a tensile stress of 347 MPa (50330 psi) during use, determine the minimum length of a surface crack that will lead to fracture. Assume a value of 0.94 for Y. mm
3. A structural component is fabricated from an alloy that has a plane-strain fracture toughness of...
3. A structural component is fabricated from an alloy that has a plane-strain fracture toughness of 69 MPa, m (69 MPa square root of "m"). It has been determined that this component fails at a stress of 250 MPa when the maximum length of a surface crack is 1.6 mm. What is the maximum allowable surface crack length (in mm) without fracture for this same component exposed to a stress of 250 MPa and made from another alloy that has...
Question 10 (7 marks) Suppose that a BMW car component fabricated from 4340 steel alloy having...
Question 10 (7 marks) Suppose that a BMW car component fabricated from 4340 steel alloy having a plane strain fracture toughness of 50 MPavm is exposed to a stress of 950 MPa. NDT results show there are two cracks. One is a surface crack of 0.60 mm long, and the other is an internal crack of 2 mm long. Will this component experience fracture? Why or why not? Assume that the parameter Y has a value of 1.0. Kjc: Plane...
An aircraft component is fabricated from an Al alloy that has a plane strain fracture toughness...
An aircraft component is fabricated from an Al alloy that has a plane strain fracture toughness of 32 MPa·m1/2. It has been determined that fracture results at a stress of 235 MPa when the maximum internal crack length is 1.8 mm. For the same component and alloy, will fracture occur at a stress level of 310 MPa when the maximum internal crack length is 0.9 mm?
A specimen of a 4340 steel alloy with a plane strain fracture toughness of 54.8 MPaym...
A specimen of a 4340 steel alloy with a plane strain fracture toughness of 54.8 MPaym (50 ksi n) is exposed to a stress of 1225 MPa (177700 psi). Assume that the parameter Y has a value of 1.04 (a) If the largest surface crack is 0.7 mm (0.02756 in.) long, determine the critical stress C- MPa (b) Will this specimen experience fracture?
2. An aircraft component is fabricated from an aluminum alloy that has a plane strain fracture...
2. An aircraft component is fabricated from an aluminum alloy that has a plane strain fracture toughness of 35 MPa m. It has been determined that fracture results at a stress of 250 MPa when the maximum (or critical) internal crack length is 2.0 mm. For this same component and alloy, will fracture occur at a stress level of 325 MPa when the maximum internal crack length is 1.0 mm? (10 points)
Deformation and Fracture Mechanics 1. (Fracture toughness) (a) An AISI 4340 steel plate has a width...
Deformation and Fracture Mechanics
1. (Fracture toughness) (a) An AISI 4340 steel plate has a width W of 30 cm and has a central crack 2a of 3 mm. The plate is under a uniform stress, ?·This steel has a Kic value of 50 m2. Find the maximum stress for this crack length. (b) If the operating stress is 1500 MPa, compute the maximum crack size that the steel may have without failure. 2. (Plastic zone radius) The size of...
Suppose that a wing component on an aircraft is fabricated from an aluminum alloy (E =...
Suppose that a wing component on an aircraft is fabricated from an aluminum alloy (E = 73 GPa) that has a plane-strain fracture toughness of 28.0 MPa√m. It has been determined that fracture results at a stress of 160 MPa. If we use another alloy (E = 150 GPa) with a plane-strain fracture toughness of 35.0 MPa√m, assuming that the size of the maximum internal crack is half in this new material for this same component. With appropriate calculations show...
Chapter 9 1. What is the magnitude of the maximum stress that exists at the tip of an internal cr...
Chapter 9 1. What is the magnitude of the maximum stress that exists at the tip of an internal crack having a radius of curvature of 2.5 x 10-4 mm (10-5 in.) and a crack length of 2.5 x 10-2 mm (10-3 in.) when a tensile stress of 170 MPa (25,000 psi) is applied? 2. A large plate is fabricated from a steel alloy that has a plane strain fracture toughness of 55 MPa m (50 ksi in.). If the plate is...
1. AA 6061, a high-strength aluminum alloy, has a 0.2% offset yield strength of 37,500-psi and...
1. AA 6061, a high-strength aluminum alloy, has a 0.2% offset yield strength of 37,500-psi and a plane strain fracture toughness (Kic) 26,400-psi (inch) At a service stress equivalent to 80% of the yield strength, will this structure fracture if it contains an edge crack of length 2.24-inches. Assume that the geometric factor, f, is 1.12. 2. A steel alloy, which has a plane strain fracture toughness (Kle) of 49-MPa(m) is exposed to a service stress of 1010-MPa. Is fracture...
A large plate is fabricated from a steel alloy that has a plane strain fracture toughness of 75 MPam (68.25 ksi vin.). If the plate is exposed to a tensile stress of 347 MPa (50330 psi) during use, determine the minimum length of a surface crack that will lead to fracture. Assume a value of 0.94 for Y. mm
3. A structural component is fabricated from an alloy that has a plane-strain fracture toughness of 69 MPa, m (69 MPa square root of "m"). It has been determined that this component fails at a stress of 250 MPa when the maximum length of a surface crack is 1.6 mm. What is the maximum allowable surface crack length (in mm) without fracture for this same component exposed to a stress of 250 MPa and made from another alloy that has...
Question 10 (7 marks) Suppose that a BMW car component fabricated from 4340 steel alloy having a plane strain fracture toughness of 50 MPavm is exposed to a stress of 950 MPa. NDT results show there are two cracks. One is a surface crack of 0.60 mm long, and the other is an internal crack of 2 mm long. Will this component experience fracture? Why or why not? Assume that the parameter Y has a value of 1.0. Kjc: Plane...
A specimen of a 4340 steel alloy with a plane strain fracture toughness of 54.8 MPaym (50 ksi n) is exposed to a stress of 1225 MPa (177700 psi). Assume that the parameter Y has a value of 1.04 (a) If the largest surface crack is 0.7 mm (0.02756 in.) long, determine the critical stress C- MPa (b) Will this specimen experience fracture?
2. An aircraft component is fabricated from an aluminum alloy that has a plane strain fracture toughness of 35 MPa m. It has been determined that fracture results at a stress of 250 MPa when the maximum (or critical) internal crack length is 2.0 mm. For this same component and alloy, will fracture occur at a stress level of 325 MPa when the maximum internal crack length is 1.0 mm? (10 points)
Deformation and Fracture Mechanics
1. (Fracture toughness) (a) An AISI 4340 steel plate has a width W of 30 cm and has a central crack 2a of 3 mm. The plate is under a uniform stress, ?·This steel has a Kic value of 50 m2. Find the maximum stress for this crack length. (b) If the operating stress is 1500 MPa, compute the maximum crack size that the steel may have without failure. 2. (Plastic zone radius) The size of...
Chapter 9 1. What is the magnitude of the maximum stress that exists at the tip of an internal crack having a radius of curvature of 2.5 x 10-4 mm (10-5 in.) and a crack length of 2.5 x 10-2 mm (10-3 in.) when a tensile stress of 170 MPa (25,000 psi) is applied? 2. A large plate is fabricated from a steel alloy that has a plane strain fracture toughness of 55 MPa m (50 ksi in.). If the plate is...
1. AA 6061, a high-strength aluminum alloy, has a 0.2% offset yield strength of 37,500-psi and a plane strain fracture toughness (Kic) 26,400-psi (inch) At a service stress equivalent to 80% of the yield strength, will this structure fracture if it contains an edge crack of length 2.24-inches. Assume that the geometric factor, f, is 1.12. 2. A steel alloy, which has a plane strain fracture toughness (Kle) of 49-MPa(m) is exposed to a service stress of 1010-MPa. Is fracture...
Most questions answered within 3 hours.
-
An individual who has automobile insurance from a certain
company is randomly selected. Let Y be...
asked 11 minutes ago -
Initial mean=6600 and median = 1500, after 2 data sets removed,
new mean = 1850 and...
asked 12 minutes ago -
A 3330-kg spacecraft is in a circular orbit 2770 km above the
surface of Mars.
How...
asked 11 minutes ago -
The outcome X of an experiment has only two possible values, X=4
and X=5. Given that...
asked 13 minutes ago -
When UV light of wavelength 288 nm falls on a metal surface, the
maximum kinetic energy...
asked 23 minutes ago -
Your company has just brought in a new line of products... And
they are pieces of...
asked 26 minutes ago -
in three paragraphs or more discuss the role of the U.S.
Children’s Bureau in dealing with...
asked 25 minutes ago -
Place the following salts in order of increasing water
solubility:
i. Fe(OH)2 Ksp = 7.9 ×...
asked 29 minutes ago -
If inflation is increasing at 2.6 percent per year, and your
salary increases at the same...
asked 29 minutes ago -
An aspirin dose of 5.0mg per kg of body weight has been
prescribed to reduce the...
asked 36 minutes ago -
The AASB Conceptual Framework (2.12-2.19) refers to ‘faithful
representation’ as being necessary for financial information to...
asked 41 minutes ago -
A U.S. corporation with net receivables in euro could hedge by
_________________.
A. buying euro forward...
asked 42 minutes ago