7) A diffractometer pattern was recorded from a strained aluminum sample (FCC, a 4.05 A) using CuKa x-rays (λ-1 .542 A). If the broadening (FWHM) of the { 331 } reflection was measured to be 1°,...
7) A diffractometer pattern was recorded from a strained aluminum sample (FCC, a 4.05 A) using CuKa x-rays (λ-1 .542 A). If the broadening (FWHM) of the { 331 } reflection was measured to be 1°, what is the magnitude of microstrain in the Al sample?
7) A diffractometer pattern was recorded from a strained aluminum sample (FCC, a 4.05 A) using CuKa x-rays (λ-1 .542 A). If the broadening (FWHM) of the { 331 } reflection was measured to be 1°, what is the magnitude of microstrain in the Al sample?