Consider the following three alloys from the Al-Cu system (see Al-Cu Phase Diagram): Pure Aluminum, 3wt%Cu-97wt%Al, and 8wt%Cu-92wt%Al. • Which of these alloys is the best candidate for Age Hardening? Why?• Which of these alloys is the worst candidate forAge Hardening? Why?
Please
dear thumpsup for the answer. Thank you. I am pretty sure of the
choice.
Consider the following three alloys from the Al-Cu system (see Al-Cu Phase Diagram): Pure Aluminum, 3wt%Cu-97wt%Al,...
Assignment Details Aluminium alloys are very widely used in the industry as structural metals, second only to steel. Pure aluminium is very soft, light in weight and low melting point which makes it quite popular for various applications. However, adding alloying elements to aluminium enhances various physical properties making it even stronger and versatile for numerous engineering applications. Answer the following questions 1. Identify the following information for pure aluminium: Atomic number Atomic mass Atomic radius Crystal structure Density Periodic...
The Al-Cu equilibrium phase diagram is reported below. For age hardening the alloy containing 4% of Cu: 700 (660 L 600 a+ @+L O 5.65 $25 500 Temperature (°C) 400 + 300 200 AI 10 20 30 40 SO Weight percent copper Select one: O a. a microstructure consisting of alpha phase with theta phase precipitated at grain boundaries must be obtained b. initially the alloy must be first solution annealed at 550 °C and then quenched down to room...
• It is a eutectic system. • The melting point of pure aluminum is 6600C • The melting point of silicon is 1410 0C • The eutectic temperature is 5800C • Aluminum is insoluble in silicon • The eutectic composition is 85% Al + 15% Si • The Al-rich phase (α) is a solid solution of Si in Al and the maximum solubility of Si in α is 3% at the eutectic temperature • At 500°C the solubility of Si in α has fallen to 0% and...
2) From the Cu-Ag phase diagram, determine the melting temperature of pure Cu and pure Ag. Determine also the eutectic temperature. 3) There are two liquidus line on the phase diagram. Let us assume that you have measured several cooling curves of samples covering from 0-100 wt% Ag composition range. The data points (phase transition points) on both liquidus lines are determined as in the following table: Left liquidus line Right liquidus line Wt% Ag Temperature (°C) Wt% Ag Temperature...
Material Science!!!
The Cu-Sn phase diagram has historical significance as this alloy is known as bronze. The ability to make a bronze alloy changed civilization since bronze has a higher yield strength than pure copper. Cu-Sn alloys also have modern applications in electronics as a basis for the replacement of lead based solders. Answer the following questions, relative to this diagram What is the melting point of pure Cu? What is the melting point of pure Sn? What is the...
In the Al-Cu phase diagram, determine what phases are present
in the binary areas (white area).
Determine all the phase transformations happened in the
following phase diagram.
For a 20 wt% Cu alloy at 500 oC, determine: The phases
present
The phase compositions
The fraction of each phase
Draw microstructure of this alloy at 700 oC, 560 oC and 300
oC.
We are interested to design an alloy with heat treatable
characteristics. Please suggest a composition range and explain
why?...
Additional Problem 1: Consider the following binary phase diagram for the Cu-Ni system at 1 atm pressure (a) For XNfotal 0.3 at 1500 K, find XNt and Xw°, and estimate f and f (b) Starting from XNfotal = 0.3 at 1500 K, the system is cooled, and a (Cu,Ni) solid solution forms. Find XNi for the last drop of the liquid as it crystallizes Ni 10 TГ Cu - Ni 20 30 40 50 60 70 80 90 wt% 1800...
5. Part of the Al-Cu phase diagram is shown below. Consider an AI-33 wt% Cu alloy which has been solidified 800 700 660°C 600 548°C 02 3% 500 - 400 300 200 10 20 40 50 70 30 60 Al Wt % Cu a) What phases would be present after solidification and cooling to room temperature? b) What compositions would those phases have? c) Calculate the relative amounts of those phases d) Below is a micrograph for the solidified Al-33...
Question: Create Young’s modulus-melting point (E-Tm)
chart (level 2) for metals and alloys. Use ‘guideline’ function to
determine which slope among 0.5, 1 and 2 in the E-Tm
chart best describes the dependence between E and Tm.
Justify this dependence from the origin of these two
properties.
I had already drawn the picture. Could you explain the
reason why Yong's modulus and melting point have a linear
relationship? Justify this dependence from the origin of these two
properties.!!!!
- 0...
2. [25 points] The following figure shows the phase diagram of Cu-Ag alloy system. A mixture of Ag and Cu with a eutectic composition (or concentration) is heated to a high temperature and keep for enough time to prepare the material into a uniform liquid state. The material is then cooled down to 800°c. Cu-Ag System 1200 Liquid 800 A 600 400 100 80 60 40 20 wt% Ag a) What is the Ag composition in the original material so...