Binary eutectic phase diagram describes chemical behavior of two immiscible components from completely mixable components. On abscissa( x - axis) we plot composition of components and ordinate (y-axis) variation of temperature. The line R is liquidus which separate all melt components to melt + crystal components (chemical). The line P is eutectic temperature. And Q line is eutectic composition of components.
so the correct answer is
R line- liquidus
P line - eutectic temperature
Q line - eutectic composition
The figure shows Binary eutectic phase diagram of two alloy components A and B. The entities...
URGENT Question 3 Consider a binary eutectic phase diagram, shown in the figure below, where substances A and B, which have partial solubility within each other in the solid state, will form the solid a and solid B solution phases. See the eutectic phase diagram containing the partial resolution and explain in detail the phases obtained by drawing the change graphs of the mixture with the mixture of Gibbs free energy at different temperatures. Constants: R=2 cal/molK= 8.32 J/molK=0.082 liter...
2. [25 points] The following figure shows the phase diagram of Cu-Ag alloy system. A mixture of Ag and Cu with a eutectic composition (or concentration) is heated to a high temperature and keep for enough time to prepare the material into a uniform liquid state. The material is then cooled down to 800°c. Cu-Ag System 1200 Liquid 800 A 600 400 100 80 60 40 20 wt% Ag a) What is the Ag composition in the original material so...
Consider the hypothetical eutectic phase diagram for metals A and B, which is similar to that for the lead-tin system, (shown in the figure below.) Assume that (1) O and S phases exist at the A and B extremities of the phase diagram, respectively; (2) the eutectic composition is 36 wt% A-64 wt% B, and (3) the composition of the phase at the eutectic temperature is 88 wt% A-12 wt% B. Determine the composition of an alloy that will yield...
3. On Silver-Copper phase diagram, label the liquidus line, eutectic point, and all unlabeled regions. Also answer questions below a. How many phases are there? b. What is the eutectic temperature? c. What is the eutectic concentration (in mass percent)? d. What is the composition of the Ag in the solid solution at the eutectic temperature? e. What is the composition of the Cu in the solid solution at the eutectic temperature? f. At 600°C what is the composition of...
In the following phase diagram for Zn-Cu Alloy. Label one eutectic, eutectoid and peritectic point and write down the reactions and all other relevant details. Also explain the eutectoid reaction i.e. why does one solid phase convert to two solid phases as the alloy cools down. a)The figure needs to be part of your answer sheet Composition (at% Zn) 0 20 40 60 80 1200 100 12200 2000 a + L Liquid 1000 1800 B+L 1600 800 + 1400 B...
10. In the following phase diagram for Zn-Cu Alloy. Label one eutectic, eutectoid and peritectic point and write down the reactions and all other relevant details. Also explain the eutectoid reaction i.e. why does one solid phase convert to two solid phases as the alloy cools down.....(5 points) a)The figure needs to be part of your answer sheet Composition (at% Zn) 20 1200 40 60 100 12200 80 2000 a+L Liquid 1000 1800 B+L 1600 800 1400 3 B Temperature...
10. In the following phase diagram for Zn-Cu Alloy. Label one eutectic, eutectoid and peritectic point and write down the reactions and all other relevant details. Also explain the eutectoid reaction i.e. why does one solid phase convert to two solid phases as the alloy cools down.....(5 points) a)The figure needs to be part of your answer sheet Composition (at% Zn) 20 40 60 80 1200 100 2200 2000 a + L Liquid 1000 1800 B+L 1600 800 1400 €...
2. [25 points] The following figure shows the phase diagram of Cu-Ag alloy syst em. A mixture of Ag and Cu with a eutectic composition (or concentration) is heated to a high temperature and keep for enough time to prepare the material into a uniform liquid state. The material is then cooled down to 800°C. Cu-Ag System 1200p Liquid 1000 800 A B. 600 400 200 100 80 60 40 20 wt% Ag (o) What is the Ag composition in...
10. In the following phase diagram for Zn-Cu Alloy. Label one eutectic, eutectoid and peritectic point and write down the reactions and all other relevant details. Also explain the eutectoid reaction i.e. why does one solid phase convert to two solid phases as the alloy cools down.....(5 points) Composition (at% Zn) 20 40 60 80 12000 100 2200 2000 a + L a+2 Liquid 1000 1800 BUL 1600 800 a 1400 B Temperature (°C) a Temperature (°F) B 8 +L...
10. In the following phase diagram for Zn-Cu Alloy. Label one eutectic, eutectoid and peritectic point and write down the reactions and all other relevant details. Also explain the eutectoid reaction i.e. why does one solid phase convert to two solid phases as the alloy cools down.....(5 points) Composition (at% Zn) 20 40 60 80 12000 100 2200 2000 a + L a+2 Liquid 1000 1800 BUL 1600 800 a 1400 B Temperature (°C) a Temperature (°F) B 8 +L...