2. For the Cu-Ag phase diagram, answer the following. Label the figure and add is part...
For the Cu-Ag phase diagram, answer the following. Label the figure and add is part of your answer sheet........ ...(11 points) a) What is the eutectic temperature and composition? (1 point) b) In the context of this diagram, what does the symbol B represent? (1 point) c) Assume slow cooling and that equilibrium conditions exist for the alloy for 70 wt% Ag – 30 wt% Cu. If this is being cooled from 1000 °C, when will the first solid form...
For the Cu-Ag phase diagram, answer the following. Label the figure and add is part of your answer sheet………………………….(11 points) What is the eutectic temperature and composition? (1 point) In the context of this diagram, what does the symbol β represent? (1 point) Assume slow cooling and that equilibrium conditions exist for the alloy for 70 wt% Ag – 30 wt% Cu. If this is being cooled from 1000 °C, when will the first solid form and what composition would...
2. For the Cu-Ag phase diagram, answer the following. Label the figure and add is part of your answer sheet....... .........(11 points) a) What is the eutectic temperature and composition? (1 point) b) In the context of this diagram, what does the symbol B represent? (1 point) c) Assume slow cooling and that equilibrium conditions exist for the alloy for 70 wt% Ag - 30 wt% Cu. If this is being cooled from 1000 °C, when will the first solid...
For the Cu-Ag phase diagram, answer the following. Label the figure and add is part of your answer sheet………………………….(11 points) What is the eutectic temperature and composition? (1 point) In the context of this diagram, what does the symbol β represent? (1 point)
2. For the CA phase diagram, answer the following Label the figure and add is part of your answer sheet a) What is the cutectie temperature and compositi? (point) b) In the context of this diagram, what does the symbol report pasi c) Assume slow cooling and that equilibrium conditions exist for the alley face this is being cooled from 1000" when will the first solid form and what composite would the solid have points) 1) At the same composition...
1. For the Cu-Zn phase diagram. For a 68 wt% Zn-32 wt% Cu alloy, list the phases and compositions that exist at 1000 °C, 760 °C, 600 °C and 400 °C. 2. For the Cu-Ag phase diagram, answer the following. Label the figure and add is part of your answer sheet.. .....(11 points) a) What is the eutectic temperature and composition? (1 point) b) In the context of this diagram, what does the symbol ß represent? (1 point) Composition (at%...
3. On Silver-Copper phase diagram, label the liquidus line, eutectic point, and all unlabeled regions. Also answer questions below a. How many phases are there? b. What is the eutectic temperature? c. What is the eutectic concentration (in mass percent)? d. What is the composition of the Ag in the solid solution at the eutectic temperature? e. What is the composition of the Cu in the solid solution at the eutectic temperature? f. At 600°C what is the composition of...
2. [25 points] The following figure shows the phase diagram of Cu-Ag alloy system. A mixture of Ag and Cu with a eutectic composition (or concentration) is heated to a high temperature and keep for enough time to prepare the material into a uniform liquid state. The material is then cooled down to 800°c. Cu-Ag System 1200 Liquid 800 A 600 400 100 80 60 40 20 wt% Ag a) What is the Ag composition in the original material so...
2. [25 points] The following figure shows the phase diagram of Cu-Ag alloy syst em. A mixture of Ag and Cu with a eutectic composition (or concentration) is heated to a high temperature and keep for enough time to prepare the material into a uniform liquid state. The material is then cooled down to 800°C. Cu-Ag System 1200p Liquid 1000 800 A B. 600 400 200 100 80 60 40 20 wt% Ag (o) What is the Ag composition in...
Composition (at% Ag) 0 20 40 60 80 100 2200 1200 A 2000 -Liquidus 1000 Liquid 1800 F Solidus a + L 1600 a 800 779°C (TE) BUL B E G 1400 8.0 (C&E) Temperature (°C) 71.9 (CE) B 91.2 (CBE) Temperature (°F) 1200 600 1000 Solvus a + B 800 400 с 600 H 200 400 100 0 20 40 60 80 (Cu) Composition (wt% Ag) (Ag) c) Assume slow cooling and that equilibrium conditions exist for the alloy...