A tensile force of 1,216 lbs is applied to a 10.4 inch long bar that is 0.500 inches in diameter. Use a modulus of elasticity of 15,000,000 psi to calculate the change in length of the bar.
Please
dear thumpsup for the answer. Thank you
A tensile force of 1,216 lbs is applied to a 10.4 inch long bar that is...
1. A tensile force of 100 kN is applied on a 0.02 m diameter 2 m length rod. After applying the load, the diameter of the rod decreases to 0.01998 m and the length increases to 2.01 m. What is the Poisson's Ratio of this material? 2. A tensile force of 100 kN is applied on a 0.02 m diameter 2 m length rod. After applying the load, the diameter of the rod decreases to 0.01998 m and the length...
(a) A wood bar is subjected to tensile force of 60 kips at two ends. It is 5 ft long, and has the rectangular Cross section which height is 4 in, and width is 2 in. The modulus of elasticity is 1.9×103ksi. Determine the total clastic deformation of the wood bar. Answer in the unit of inches, to 0.001. Note: 1 ft = 12 in., 1 ksi = 1000 psi. (b) If this wood bar has a hole with a diameter...
1. A tensile test was performed using a standard 0.505 in. diameter specimen (Do 0.505 in) of 4140 steel with 2 inch initial gage length (Lo 2.00 in), and the following were determined: . Elastic Modulus (E)-30 x 106 psi Yield Strength (To) = 60,000 psi Strain at maximum load = 0.15 .Breaking Load (Pbreak) 15,000 lbs Maximum Load (Pa) 20,000 lbs 0 % Elongation-25% . a. (3 points) Calculate the stress at the break point: b. (5 points) Calculate...
question 1 and 2 please
1. A one-inch diameter steel rod is used as a pin-pin connected compression member. Calculate the critical load using Euler's formula. The proportional limit for the steel is 36,000 psi and the modulus of elasticity is 30,000,000 psi, (the radius of gyration for a circular section is d/4). Assume the length of the rod to be: A. 1.5 feet B. 4.5 feet Comment on the results of A and B. 2. A one-inch diameter steel...
A tensile force of 120 kN is applied on a 0.02-m diameter and
2-m long rod. After applying the load, the diameter of the rod
decreases to 0.01998 m and the length increases to 2.01 m. The
engineering stress on that rod is most nearly:
PLEASE SHOW ALL WORK.
A tensile force of 120 leN is applied on a 0.02-m diameter and 2-mm long rod. After applying the load, the diameter of the rod decreases to 0.01998 m and the...
A flat 1018 steel sample was tested in a tensile machine. Sample dimensions are width = 0.425 inch, thickness = 0.175 inch, original gauge length = 3.45 inch. The sample shows yielding when 3300 lb force is applied with a corresponding change in length of 0.06 inch. From the data, the greatest force applied during testing was 4500 lbs and the sample had elongated by total of 0.5 inch. At fracture, the force applied to the sample decreased to 3000...
2. A round tube of diameter 2 inches is welded to a wall and subjected to a tensile force of 5000 lbs as shown. The weld rod is E60. The weld leg is 0.25 inches. What is the factor of safety guarding against weld metal yielding as a result of this force? a) 1.62 b) 2.48 c) 3.38 d) 4.13 e) None of these lbs F 5000
2. A round tube of diameter 2 inches is welded to a wall...
1. The circular bar has a length of 12 ft-o in., a diameter of 1 in., and a modulus of elasticity E = 29x10 psi. It is subjected to an axial force of 10,000 lbs along the centroidal axis of the bar's cross-sectional area as shown. Find the following: (i) Average normal stress and average shear stress at section a-a (ii) Average normal stress and average shear stress at section b-b (iii) The bar total elongation 10,000 lbs 10,000 lbs...
1.75 inch dia hole in a .75 inch plate of A36 steel. A force of 34000 lbs vertical to plane is applied to the hole. Use bearing stress to determine stress placed vertical to the plane and at 45 degrees to the plane
A bar of metal (length L =200 mm, diameter d=10 mm) is loaded axially by a tensile force P = 12 kN. If the bar elongates by 0.3 mm, what is the decrease in diameter d? What is the value of modulus of elasticity? Consider, v=0.30.