Brass bushings have a length of 10 cm, inside diameter of 12 cm, and wall thickness of 4 cm; a density of brass is 8.62 gcm-3. A manufacturer plans to use a centrifugal casting method for making the bushings.
a. Name an appropriate centrifugal casting process for making the bushings.
b. Determine the rotational speed that obtains a G-factor (GF) of 70.
c. When operating at this speed, determine the centrifugal force per square meter (Pa) imposed by the molten metal on the inside wall of the mould.
We need at least 10 more requests to produce the answer.
0 / 10 have requested this problem solution
The more requests, the faster the answer.
Brass bushings have a length of 10 cm, inside diameter of 12 cm, and wall thickness...
Plz answer 3.3 and 3.4 Question 3 10 Marks During laboratory testing of a thin-wall pressure vessel, the cylinder diameter and thickness were at 10 different locations: the resulting data were as follows If the pressure inside the vessel is measured to be P - 1 mPa (mega Pascal) with an estimated uncertainty of up-+ 6 kPa (kilo Pascal, for 95% confidence interval, the tangential or hoop stress in the vessel is given by ơe-- 3.1 Compute the uncertainty in...
The cylindrical pressure vessel shown in the figure has an inside diameter of 980 mm and a wall thickness of 12 mm. The cylinder is made of an aluminum alloy that has an elastic modulus of E = 72 GPa and a shear modulus of G = 27.5 GPa. Two strain gages are mounted on the exterior surface of the cylinder at right angles to each other. The angle θ is 21°. If the pressure in the vessel is 1.86...
summatize the following info and break them into differeng key points. write them in yojr own words apartus 6.1 Introduction—The design of a successful hot box appa- ratus is influenced by many factors. Before beginning the design of an apparatus meeting this standard, the designer shall review the discussion on the limitations and accuracy, Section 13, discussions of the energy flows in a hot box, Annex A2, the metering box wall loss flow, Annex A3, and flanking loss, Annex...