QUESTION 12 A cylindrical specimen of a metal with with Elastic Modulus. E-69 GPa and Poisson...

Question

Question

Answer 1

Answer #1

longitudinal strain = P P = 56.6*103N А Е A- A d² E = 56.6*103 E = 69x109 No2 1 x (02)² x 69x109 E = 2.61 X10? u= - lateral s

Answer 2

Similar Homework Help Questions

A cylindrical bar of metal having a diameter of 16.5 mm and a length of 183...

A cylindrical bar of metal having a diameter of 16.5 mm and a length of 183 mm is deformed elastically in tension with a force of 42000 N. Given that the elastic modulus and Poisson's ratio of the metal are 67.1 GPa and 0.34, respectively, determine the following:(a) The amount by which this specimen will elongate (in mm) in the direction of the applied stress. (b) The change in diameter of the specimen (in mm). Indicate an increase in diameter...
Problem #1 A cylindrical rod of copper (E 110 GPa) having a yield strength of 240...

Problem #1 A cylindrical rod of copper (E 110 GPa) having a yield strength of 240 MPa is to be subjected to a load of 6660 N. If the length of the rod is 380 mm, what must the diameter be to allow an elongation of 0.50 mm? A cylindrical specimen of some alloy 8 mm in diameter is stressed elastically in tension. A force of 15,700 N produces a reduction in the specimen diameter of 5 10-3 mm. Compute...
A cylindrical bar of metal having a diameter of 19.0 mm and a length of 207...

A cylindrical bar of metal having a diameter of 19.0 mm and a length of 207 mm is deformed elastically in tension with a force of 53700 N. Given that the elastic modulus and Poisson's ratio of the metal are 67.6 GPa and 0.34, respectively, determine the following: (a) The amount by which this specimen will elongate in the direction of the applied stress.

A cylindrical bar of metal having a diameter of (4.726x10^0) mm and a length of (6.0264x10^2)...

A cylindrical bar of metal having a diameter of (4.726x10^0) mm and a length of (6.0264x10^2) mm is deformed elastically in tension with a force of (1.16x10^4) N. Given that the elastic modulus and Poisson's ratio of the metal are (1.3007x10^2) GPa and (3.3600x10^-1) , respectively, determine the change in diameter of the specimen (in mm). Indicate an increase in diameter with a positive number and a decrease with a negative number. As always use scientific notation in the form...
A cylindrical specimen of some metal alloy having an elastic modulus of 121 GPa and an...

A cylindrical specimen of some metal alloy having an elastic modulus of 121 GPa and an original cross-sectional diameter of 4.7 mm will experience only elastic deformation when a tensile load of 2400 N is applied. Calculate the maximum length of the specimen before deformation if the maximum allowable elongation is 0.41 mm.
A cylindrical specimen of some metal alloy having an elastic modulus of 120 GPa and an...

A cylindrical specimen of some metal alloy having an elastic modulus of 120 GPa and an original cross-sectional diameter of 3.0 mm will experience only elastic deformation when a tensile load of 2400 N is applied. Calculate the maximum length of the specimen before deformation if the maximum allowable elongation is 0.47 mm.

Problem 7.17 A cylindrical specimen of some metal alloy 11.0 mm (0.4331 in.) in diameter is...

Problem 7.17 A cylindrical specimen of some metal alloy 11.0 mm (0.4331 in.) in diameter is stressed elastically in tension. A force of 14300 N (3215 lbf) produces a reduction in specimen diameter of 7 × 10-3 mm (2.756 × 10-4 in.). Compute Poisson's ratio for this material if its elastic modulus is 100 GPa (14.5 × 106 psi).
Problem 6.17 A cylindrical specimen of some metal alloy 10.3 mm (0.4055 in.) in diameter is...

Problem 6.17 A cylindrical specimen of some metal alloy 10.3 mm (0.4055 in.) in diameter is stressed elastically in tension. A force of 14800 N (3327 lbf) produces a reduction in specimen diameter of 5x 10-3 mm (1.969 x10-4 in.). Compute Poisson's ratio for this material if its elastic modulus is 100 GPa (14.5x 106 ps the tolerance is +/-290
A cylindrical specimen of some metal alloy 6.8 mm in diameter is stressed in tension. A...

A cylindrical specimen of some metal alloy 6.8 mm in diameter is stressed in tension. A force of 1720 N produces an elastic reduction in specimen diameter of 0.0044 mm. Calculate the elastic modulus (in GPa) of this material if its Poisson's ratio is 0.35.

Material Science and Engineering (Help me please Immediately)4

4. A cylindrical aluminum specimen having a diameter of \(20 \mathrm{~mm}\) and length of \(210 \mathrm{~mm}\) is deformed elastically in tension with a force of \(48,800 \mathrm{~N},\left(\mathrm{U}_{\mathrm{A} 1}=0.33, \mathrm{E}_{\mathrm{Al}}=69 \mathrm{GPa}\right)\)Determine the following:(a) The amount by which this specimen will elongate in the direction of the applied stress.(b) The change in diameter of the specimen. Will the diameter increase or decrease?