A metal wire having a diameter of 1.1390 mm and a length of 514.1 mm is...
A cylindrical bar of metal having a diameter of (4.726x10^0) mm and a length of (6.0264x10^2) mm is deformed elastically in tension with a force of (1.16x10^4) N. Given that the elastic modulus and Poisson's ratio of the metal are (1.3007x10^2) GPa and (3.3600x10^-1) , respectively, determine the change in diameter of the specimen (in mm). Indicate an increase in diameter with a positive number and a decrease with a negative number. As always use scientific notation in the form...
A cylindrical bar of metal having a diameter of 16.5 mm and a length of 183 mm is deformed elastically in tension with a force of 42000 N. Given that the elastic modulus and Poisson's ratio of the metal are 67.1 GPa and 0.34, respectively, determine the following:(a) The amount by which this specimen will elongate (in mm) in the direction of the applied stress. (b) The change in diameter of the specimen (in mm). Indicate an increase in diameter...
No. 5 (20 points) (a) Determine the time necessary to achieve a carbon concentration of 0.30 wt.% at a position of 4 mm into an iron-carbon alloy that initially contains 0.10 wt. % C. The surface concentration is to be maintained at 0.90 wt.% C, and the diffusion coefficient of C is 7.0 x 10-11 m2/sec. (10 points) (b) The diffusion coefficient of Ni in a stainless steel (fcc) is 1 x 1022 m2/sec at 500°C and 1 x 10-15...
9. (4 Marks) A sheet of steel 3 mm thick has nitrogen atmospheres on both sides at 900°C and is permitted to achieve a steady-state diffusion condition. The diffusion coefficient for nitrogen in steel at this temperature is 1.85 x 10-10 m2/s, and the diffusion flux is found to be 1.0 x 10-7 kg/m2.s. Also, it is known that the concentration of nitrogen in the steel at the high-pressure surface is 2 kg/m3. How far into the sheet from this...
A cylindrical bar of metal having a diameter of 19.0 mm and a length of 207 mm is deformed elastically in tension with a force of 53700 N. Given that the elastic modulus and Poisson's ratio of the metal are 67.6 GPa and 0.34, respectively, determine the following: (a) The amount by which this specimen will elongate in the direction of the applied stress.
A sheet of steel 1.7 mm thick has nitrogen atmospheres on both sides at 1200°C and is permitted to achieve a steady-state diffusion condition. The diffusion coefficient for nitrogen in steel at this temperature is 6.8 x 10-11 m/s, and the diffusion flux is found to be 1.4 x 10 kg/m2-s. Also, it is known that the concentration of nitrogen in the steel at the high-pressure surface is 5.5 kg/m. How far into the sheet from this high-pressure side will...
Problem 5.09 A sheet of steel 3.6 mm thick has nitrogen atmospheres on both sides at 1200°C and is permitted to achieve a steady-state diffusion condition. The diffusion coefficient for nitrogen in steel at this temperature is 6.9 x 10-11 m2/s, and the diffusion flux is found to be 3.9 x 10 kg/m2-s Also, it is known that the concentration of nitrogen in the steel at the high-pressure surface is 4.7 kg/m3. How far into the sheet from this high...
A sheet of steel 2.2 mm thick has nitrogen atmospheres on both sides at 1200°C and is permitted to achieve a steady-state diffusion condition. The diffusion coefficient for nitrogen in steel at this temperature is 6.8 × 10-11 m2/s, and the diffusion flux is found to be 2.5 × 10-7 kg/m2-s. Also, it is known that the concentration of nitrogen in the steel at the high-pressure surface is 5.1 kg/m3. How far into the sheet from this high-pressure side will...
A sheet of steel 3.8 mm thick has nitrogen atmospheres on both sides at 1200°C and is permitted to achieve a steady-state diffusion condition. The diffusion coefficient for nitrogen in steel at this temperature is 5.1 × 10-11 m2/s, and the diffusion flux is found to be 4.8 × 10-7 kg/m2-s. Also, it is known that the concentration of nitrogen in the steel at the high-pressure surface is 4.7 kg/m3. How far into the sheet from this high-pressure side will...
5.09 Problem 5.09 A sheet of steel 1.5 mm thick has nitrogen atmospheres on both sides at 12 OC and is permitted to achieve a steady-state diffusion condition. The diffusion coefficient for nitrogen in steel at this temperature is 5.5 × 10-11 m2/s and the diffusion flux s found to be 4.)× 10 7 kg/m2-s Also, t is known that the concentration of nit ogen in the steel at the high pressure surface s 60 kg m3 Ho far into...