1) Useful parameters for CdTe a. ni- 1e8 cm 3 2) kT 25.8mev Problem #1 (100 points) Consider an ideal, long-diode type solar cell made of a CdTe abrupt asymmetrical PN junction. The relevant properti...
Problem 4: Narrow-Base Diode Consider an ideal pn* step-junction Si diode maintained at 300K with cross-sectional area A = 104cm2. The doping concentration on the p-type side is Na= 1017 cm3 (uncompensated). (The n-type side is degenerately doped.) The electron recombination lifetime in the p-type region is tn = 10-6 s. The width of the quasi-neutral p-type region is 1 um, for VA=0 V. a Is this a narrow-base diode? Justify your answer. b) Calculate the diode saturation current Io....
Problem 3 (25 points) Consider a silicon pn junction at T - 300 K, NA- 1016 cm3, ND-5x1016 cm-3. The minority carrier lifetimes are τα , τ,-1 us. The junction is forward biased with Va-0.5V The minority carrier diffusion coefficients are D 25 cm/s, Da- 10 cm2/s n,1.5x1010 cm3 kT 0.0267 Depletion region p-type n-type a) (5 points) Calculate the excess electron concentration as a function of x in the p-side (see the figure above) b) (10 points) Calculate the...
Problem 1 (25 points) Consider a silicon pn junction with a cross section area of 1x105 cm, a forward bias Va 0.5V, and the following parameters at T- 300K: 16cm-3 15 3 -6 KT n: 1.5x100 cm", ε' = 1 1 .7x 8.854x 10-14 Flon;ー-0.025 V Assume the critical field to be equal to 3x105 V/cm. a) (5 points) Compare the hole density at xn to the electron density at-Xp b) (5 points) Compare the hole current at xn to...