Let the tension member in Problem 15.8 be made of AISI 403 stainless steel. If the axial load P is increased to failure, will the failure be brittle fracture? What is the lower limit for the failure load?
Problem 15.8
A 2024-T851 aluminum, alloy pipe is used as a tension member. The pipe has an outside diameter of 100 mm and wall thickness of 8.0 mm. An inspection of the pipe locates a circumferential through-thickness crack having a length of 15.0 mm (Case 3 of Table 15.2). If the axial load P is increased to failure, will the failure be brittle fracture? What is the failure load?
Case 3 of Table 15.2:
TABLE 15.2 Stress Intensity Factors KI
Case 3: Central crack in finite-width strip subjected to uniform tension at infinity | ||||||||||||||
|