as soon as possible please thank you A 25 mm diameter hole will be punched in...

Question

Question

as soon as possible please thank you

A 25 mm diameter hole will be punched in a 1.6 mm thick, 5052-0 aluminum sheet at room temperature. Sut = 190 MPa. Calculate

Answer 1

Answer #1

- 190 mpa=190x100 N/m² - 190 N/mm2 Solution Sut t = 1.6mm d = 25mm Punch force F = 0.7tl (Sut) F = 0.7x 1.68 TTx 25 x 190 F =

Answer 2

Similar Homework Help Questions

A 25 mm diameter hole will be punched in a 1.6 mm thick, 5052-0 aluminum sheet...

A 25 mm diameter hole will be punched in a 1.6 mm thick, 5052-0 aluminum sheet at room temperature. 190 MPa. Calculate the maximum punch Force. Sut
Please show Every Step and As Soon as Possible. Protective layer A 25-mm diameter, spherical fuel...

Please show Every Step and As Soon as Possible. Protective layer A 25-mm diameter, spherical fuel element (27.6 W/m·K) with a volumetric rate of generation of 15 x 106 W/m² is coated with a 1-mm thick protective layer that has a thermal conductivity of 0.375 W/m·K. If the fuel element has a surface temperature of 314.15°C, determine the temperature of the outer surface of the protective layer. 25 mm 1 mm
please answer 18.11 and 18.12 18.11 A steel ring with an outside diameter of 150 mm and an inside diameter of 100 mm...

please answer 18.11 and 18.12 18.11 A steel ring with an outside diameter of 150 mm and an inside diameter of 100 mm is shrunk onto another steel ring with an inside diameter of 50 mm. An axial force of 56,54 kN is needed to push the rings apart. Calculate the pressure at the mating surface and the shrinkage allowance given that both rings are 20 mm thick and the coefficient of friction between the mating surfaces is 0,2. Using...

Please show work. Thank you! A punch press has punches forty (40) circles that are 2...

Please show work. Thank you! A punch press has punches forty (40) circles that are 2 inches in diameter through medium carbon steel that is 0.125" thick. If six hydraulic cylinders are used to achieve this force, what diameter cylinders are required if the pump has a maximum continuous operating pressure of 3150 psi? Sheaf Strcho th 2.
Strength of materials I need a solution as soon as possible please For the system shown...

Strength of materials I need a solution as soon as possible please For the system shown in Figure (1), the bolt in C is subjected to a single shear and all other bolts are double shear. The diameter of bolt at C is 15 mm, diameter of bolt at D is 10mm and diameter of bolt A is 20mm. The allowable shear stress of bolt C is 200 MPa, allowable shear stress of bolt D is 150 MPa and allowable...
please answer as soon as possible. thank you. Please write 400+ words. Thank you very much....

please answer as soon as possible. thank you. Please write 400+ words. Thank you very much. what can you as students do to help to slow or solve climate change?

Please answer as soon as possible and watch significant figures thank you 19) What mass of...

Please answer as soon as possible and watch significant figures thank you 19) What mass of barium hydroxide, in gram, must be dissolved in 200 mL of water in order to prepare a solution at pH 10.66 (at 25°C)? 3 pts
Differential equations please solve as soon as possible thank you! 3) find gencrol soluhon

Differential equations please solve as soon as possible thank you! 3) find gencrol soluhon
please I need solution as soon as possible thank you 1. You are required to prepare...

please I need solution as soon as possible thank you 1. You are required to prepare 0.56 M of NaCl for an experiment. Determine the amount of Naci (in gram) required if you only have 350 ml of distilled water. 2. Given that there is 0.04% by volume of CO2 in the air, determine the solubility of CO2 in water at 25 °C and 1 atm (ky for CO2 in water at 25 °C = 29.76 atm/(mol/L)). Formula: n =...

Please solve as soon as possible and watch for significant figures. Thank you . AG -AG'...

Please solve as soon as possible and watch for significant figures. Thank you . AG -AG' for a reaction (A) if Q-K (b) if a-I (C) at STW al) at the start of a reaction e) at the end of a reacton